Electroluminescent device

ABSTRACT

Disclosed are electroluminescent devices that comprise organic layers that contain certain 2H-benzotriazole compounds. The 2H-benzotriazole compounds of blue-emitting, durable, organo-electrouminescent layers. The electroluminescent devices may be employed for full color display panels in for example mobile phones, televisions and personal computer screens.

The present invention relates to organo-electroluminescent (EL) devices, in particular EL devices that comprise durable, blue-emitting organo-electrouminescent layers. The organo-electroluminescent layers comprise certain 2H-benzotriazoles.

Progress has been made towards developing organic-based electroluminescent devices suitable for full color displays. Generally, an EL device is comprised of a light-emitting layer or layers and a pair of facing electrodes sandwiching the light-emitting layer(s). Application of an electric field between the electrodes results in the injection of electrons and holes to the system, resulting in the release of energy as light.

However, organo EL devices have not been developed that have suitable stability under continuous operation. In particular, there remains a need for blue-emitting, stable organo EL devices.

U.S. Pat. No. 5,104,740 teaches an electroluminescent element that comprises a fluorescent layer containing a coumarinic or azacoumarinic derivative and a hole transport layer, both made of organic compounds and laminated on top of the other. Certain of the coumarinic compounds disclosed have 2H-benzotriazole substitutents.

U.S. Pat. No. 6,280,859 discloses certain polyaromatic organic compounds for use as a light-emitting material in organo-electroluminescent devices. A 2H-benzotriazole moiety is listed among a long list of possible divalent aromatic linking groups.

U.S. Pat. No. 5,116,708 is aimed at a hole transport material for EL devices.

U.S. Pat. No. 5,518,824 teaches an EL device comprising one or more organic layers, wherein at least one of the layers is obtained by thermal or radiation-induce crosslinking. Certain benzotriazoles are disclosed as suitable charge transport compounds.

U.S. Pat. No. 4,533,612 discloses electrophotographic recording materials that comprise certain 2H-benzotriazoles as charge carrier-transporting compounds.

JP 58009151 discloses the use of certain polyaromatic benzotriazole systems in a charge transport layer of an electrophotographic photoreceptor.

U.S. Pat. No. 5,629,389 discloses an electroluminescent device having a layer that comprises 2-(2H-benzotriaol-2-yl)-4,6-bis(1-methyl-1-phenylethyl)phenol.

EP 764712 discloses ortho hydroxyphenyl-2H-benzotriazoles as stabilizers in EL devices. Tsutsui, et al., in Synthetic Metals, 1997 (85) 1201-1204, discloses 2-(2-hydroxy-5-methylphenyl)-2H-benzotriazole as a fluorescence quencher in an electron transport layer.

U.S. Pat. Nos. 2,784,183, 2,713,056, 2,784,197, 3,288,786, 3,341,530, 5,006,662, GBA-1150408, DE-A-1 052405, and DE-A-1 919181 disclose naphthobenzotriazoles used as optical brighteners.

U.S. Pat. No. 3,793,315 teaches stilbenyl benzotriazole derivatives as optical brighteners. Woessner, et al., In J. Phys. Chem., 1985 (89), 3629-3636 studied the emission of 2-(2-hydroxy-5-methylphenyl)-2H-benzotriazole, and the methoxy analogue thereof.

U.S. Pat. No. 5,486,406 teaches the use of metal complexes of ortho hydroxyphenyl-2H-benzotriazoles in organic light emitting devices.

JP 00256667 and JP 98140145 disclose metal complexes of ortho hydroxyphenyl-2H-benzotriazoles for use in electroluminescent devices.

Certain 2H-benzotriazole derivatives are found to be suitable for use in organo-electroluminescent devices. In particular, certain 2H-benzotriazole derivatives are suitable blue emitters with good durability.

The present invention is aimed at an electroluminescent device comprising an organic light-emitting layer comprising a blue-emitting 2H-benzotriazole compound.

The 2H-benzotriazole compound comprises for example one or more 2H-benzotriazole moieties:

Ar can be any form of an aromatic or heteroaromatic ring (or ring system). That is 2H-benzotriazole compound in the context of the present invention means a 2H-benzotriazole or hetero-2H-benzotriazole because Ar can be any form of an aromatic ring (not only carbons).

Examples that specify the possibilities for the

group designated above are as follows:

For example, the present 2H-benzotriazole compounds comprise one, two, three or four 2H-benzotriazole moeities. It is understood that the open valences in the 2H-benzotriazole moiety represents a covalent bond that is not limited in its substitution. According to the present invention the EL device comprise at least a 2H-benzotriazole compound, i.e. it may comprise two or more 2H-benzotriazole compounds.

The 2H-benzotriazole compound or compounds should emit light below about 520 nm, especially between about 380 nm and about 520 nm. The 2H-benzotriazole compound or compounds should have a NTSC coordinate of between about (0.12, 0.05) and about (0.16, 0.10), especially a NTSC coordinate of about (0.14, 0.08).

The 2H-benzotriazole compound or compounds should have a melting point above about 150° C., especially above about 200° C., more preferred above about 250° C., most preferred above about 300° C.

Accordingly, the present invention relates to an electroluminescent device (EL device), comprising a 2H-benzotriazole compound, especially a compound of the formula

-   a is 0, or 1, -   b is 0, or 1, -   X¹ is a group of formula     -   if b is 1, or Y³, if b is 0, wherein -   c is 0, or 1, -   X² and X³ are Independently of each other a group of formula     -   wherein d is 0, or 1, -   Ar¹, Ar², and Ar³ are independently of each other aryl or     heteroaryl, which can optionally be substituted, especially     C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be     substituted, -   Y¹ and Y² are independently of each other a divalent linking group,     and -   Y³ and Y^(3′) are Independently of each other aryl or heteroaryl,     which can optionally be substituted, especially C₆-C₃₀aryl or a     C₂-C₂₆heteroaryl, which can optionally be substituted.

In more detail, the present invention relates to an electroluminescent device, comprising a 2H-benzotriazole compound of the formula

-   Ar¹, Ar², Ar³, X², X³, Y¹ and Y² are defined as above, -   d is 0, or 1, -   Ar⁴ stand for C₆-C₃₀ aryl or a C₂-C₂₆heteroaryl, which can     optionally be substituted, and -   Y³ and Y^(3′) are independently of each other C₆-C₃₀aryl or a     C₂-C₂₆heteroaryl, which can optionally be substituted.

The groups

in formula II or III are independently of each other a group of formula

wherein

-   A²¹, A²², A²³, A²⁴, A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁷ and A¹⁸are     independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl,     C₁-C₂₄alkyl which is substituted by E and/or Interrupted by D,     C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalky, C₅-C₁₂cycloalkyl which is     substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, —NR²⁵R²⁶,     C₁-C₂₄alkylthio, —PR³²R³², C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy     which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is     substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is     substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy,     C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D,     C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E,     C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or     —CO—R²⁸, or -   A²² and A²³ or A¹¹ and A²³ are a group -    two groups A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷ and A¹⁸, which are     neighbouring to each other, are a group -    wherein A³¹, A³², A³³, A³⁴, A³⁵, A³⁶ and A³⁷ are independently of     each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is     substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl,     O₅—C₁₂cycloalkyl, O₅—C₁₂cycloalkyl which is substituted by E and/or     interrupted by S—, —O—, or —NR²⁵, C₅C₁₂cycloalkoxy,     C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl     which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which     is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy,     C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D,     C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E,     C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or     —CO—R²⁶, -   D is —CO—; —COO—; —S—; —SO—; —SO₂—; —O—; —NR²⁵; SiR³⁰R³¹; —POR³²;     CR²³═CR²⁴—; or C≡C—; and -   E is OR²⁹; —SR²⁹; —NR²⁵R²⁶; —COR²⁶; —COOR²⁷; —CONR²⁵R²⁶; —CN;     —OCOOR²⁷; or halogen; wherein -   R²³, R²⁴, R²⁵ and R²⁸ are independently of each other H; C₆-C₁₈aryl;     O₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy;     C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—; or -   R²⁵ and R²⁶ together form a five or six membered ring, in particular -   R²⁷ and R²⁸ are independently of each other H; C₆-C₁₈aryl;     C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy;     C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, -   R²⁹ is H; C₆-C₁₈aryl; C₆-C₁₈aryl, which is substituted by     C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is     interrupted by —O—, -   R³⁰ and R³¹ are independently of each other C₁-C₂₄alkyl, C₆-C₁₈aryl,     or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, and -   R³² is C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted     by C₁-C₂₄alkyl.

Preferably, the groups

are independently of each other a group of formula

-   A²¹, A²², A²³ and A²⁴ are independently of each other hydrogen,     halogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, C₆-C₁₈aryl, —NR²⁵R²⁶,     —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, especially a group of     formula -   A²² and A²³ are a group of formula -   A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷, and A¹⁸ are independently of each     other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, C₆-C₁₈aryl,     —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, wherein -   E¹ is O, S, or NR²⁵, -   R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl,     C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, R²⁷ is C₁-C₂₄alkyl.

The groups

in formula IV are independently of each other a group of formula

wherein

-   A⁴¹, A⁴², A⁴³, A⁴⁴, A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹ and     A⁶⁰ are independently of each other H, halogen, hydroxy,     C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or     interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl,     C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—,     —O—, or —NR²⁵—, NR²⁵R²⁶, C₁-C₂₄alkylthio, —PR³²R³²,     C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E,     C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl,     C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl,     C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₀-C₂₄alkoxy which is substituted by E     and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is     substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is     substituted by E, or —CO—R²⁸, or -   A⁴² and A⁴³ or A⁴² and A⁵¹ are a group -    two groups A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹ and A⁶⁰,     which are neighbouring to each other, are a group -    wherein A⁶¹, A⁶², A⁶³, A⁶⁴, A⁶⁵, A⁶⁶, A⁶⁷, A⁶⁵, A⁶⁹ and A⁷⁰ are     independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl,     C₀-C₂₄alkyl which is substituted by E and/or interrupted by D,     C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is     substituted by E and/or interrupted by S—, —O—, or —NR²⁵—,     C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E,     C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl,     C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl,     C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E     and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is     substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is     substituted by E, or —CO—R²⁶, wherein E, D, R²⁵ and R²⁶ are defined     as above and one of the substituents A⁴¹, A⁴², A⁴³, A⁴⁴, A⁵¹, A⁵²,     A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹, A⁶⁰, A⁶¹, A⁶², A⁶³, A⁶⁴, A⁶⁵,     A⁶⁶, A⁶⁶, Ar⁶⁷, A⁶⁸, A⁶⁹ and A⁷⁰ represents a single bond, i.e. the     linkage to Y².

Preferably, A⁴³ and A⁴⁴ are not a group —NR²⁵R²⁶ at the same time.

-   Y³ and Y^(3′) in formula II, IV and V are independently of each     other a group of formula -   R⁴¹, R⁴², R⁴³, R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹, R⁵², R⁵³,     R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, R⁶¹, R⁶³, R⁶⁴, R⁶⁵, R⁶⁶, R⁶⁷,     R⁷⁰, R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, R⁸⁰, R⁸¹, R⁸²,     R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, and R⁸⁷ are independently of each other H,     C₁-C₂₄alkyl, which is optionally substituted by E and/or interrupted     by D, C₁-C₂₄alkenyl, which is optionally substituted by E,     C₅-C₁₂cycloalkyl, which is optionally substituted by E,     C₅-C₁₂cycloalkoxy, which is optionally substituted by E, C₆-C₁₈aryl,     which is optionally substituted by E, C₁-C₂₄alkoxy, which is     optionally substituted by E and/or interrupted by D, C₆-C₁₈aryloxy,     which is optionally substituted by E, C₇-C₁₈arylalkoxy, which is     optionally substituted by E, C₁-C₂₄alkylthio, which is optionally     substituted by E and/or interrupted by D, C₁-C₂₄alkylselenium, which     is optionally substituted by E and/or Interrupted by D,     C₁-C₂₄alkyltellurium, which is optionally substituted by E and/or     interrupted by D, C₂-C₂₀heteroaryl which is substituted by E, or     C₆-C₁₈aralkyl, which is optionally substituted by E, or -   two groups R⁴¹, R⁴², R⁴³, R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹,     R⁵², R⁵³, R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, R⁶¹, R⁶², R⁶³, R⁶⁴,     R⁶⁵, R⁶⁶, R⁶⁷, R⁷⁰, R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁷⁷, R⁸⁰, R⁸¹,     R⁸², R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, and R⁸⁷, which are neighbouring to each     other, are a group -    wherein A⁹⁰, A⁹¹, A⁹², A⁹³, A⁹⁴, A⁹⁵, A⁹⁶ and A⁹⁷ are independently     of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is     substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl,     C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or     interrupted by S—, —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy,     C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl     which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which     is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy,     C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D,     C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E,     C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or     —CO—R²⁸, -   R⁶⁸, R⁶⁹, R⁷⁸, R⁷⁹, R⁸⁸ and R⁸⁹ are independently of each other     C₁-C₁₈ alkyl, C₁-C₂₄alkyl which is substituted by E and/or     interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E,     C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E,     C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is     substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, or -   R⁶⁸ and R⁶⁹, R⁷⁸ and R⁷⁹, and/or R⁸⁸ and R⁸⁹ form a ring, especially     a five- or six-membered ring, or R⁶⁸ and R⁷⁰, R⁶⁹ and R⁷³, R⁷⁷ and     R⁷⁸ and/or R⁸⁴ and R⁸⁹ are a group -    wherein D, E, R²⁵ and R²⁸ are defined as above.

Preferably, Y³ and Y^(3′) are independently of each other a group of formula

-   R⁴¹ is hydrogen, C₁-C₂₄alkoxy, or OC₇-C₁₈aralkyl, -   R⁴² is hydrogen, or C₁-C₂₄alkyl, -   R⁴³ is hydrogen, halogen, —CONR²⁵R²⁶, —COOR²⁷, -   E¹ is —S—, —O—, or —NR^(25′)—, wherein R^(25′) is C₁-C₂₄alkyl, or     C₆-C₁₀aryl, -   R¹¹⁰ is C₁-C₂₄alkyl, or -   R⁴² and R⁴³ are a group of formula -   R⁴⁴ is hydrogen, or C₁-C₂₄alkyl, -   R⁴⁵ is hydrogen, or C₁-C₂₄alkyl, -   A^(11′), A^(12′), A^(13′), and A^(14′) are independently of each     other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶,     —CONR²⁵R²⁶, or —COOR²⁷, -   R⁶⁸ and R⁶⁹ are independently of each other C₁-C₂₄alkyl, especially     C₄-C₁₂alkyl, especially hexyl, heptyl, 2-ethylhexyl, and octyl,     which can be Interrupted by one or two oxygen atoms, -   R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁹⁰, R⁹¹, R⁹², and R⁹³ are     independently of each other H, CN, C₁-C₂₄alkyl, C₆-C₁₀aryl,     C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, R²⁷     and R²⁸ are independently of each other H, C₆-C₁₈aryl,     C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, and R²⁷ is C₁-C₂₄alkyl.

Examples of the divalent linking groups Y¹ and Y² in formula III, IV and VI are a single bond,

-   n1, n2, n3, n4, n5, n6 and n7 are 1, 2, or 3, in particular 1, -   E¹ is —S—, —O—, or —NR^(25′), wherein R^(25′) is C₁-C₂₄alkyl, or     C₆-C₁₀aryl, -   R⁶ and R⁷ are Independently of each other H, halogen, hydroxy,     C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or     interrupted by D, C₁-C₂₄perfluoroalkyl, C₆-C₁₂cycloalkyl,     C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—,     —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is     substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E,     C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E,     C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is     substituted by E and/or interrupted by D, C₇-C₂₅aralkyl,     C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy,     C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, -   R⁸ is C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or     interrupted by D, C₆-C₂₄ aryl, or C₇-C₂₅aralkyl, -   R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, C₁-C₂₄alkyl     which is substituted by E and/or interrupted by D, C₆-C₂₄aryl,     C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl,     C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl,     C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E     and/or interrupted by D, or C₇-C₂₅aralkyl, or -   R⁹ and R¹⁰ form a ring, especially a five- or six-membered ring, -   R¹⁴ and R¹⁵ are independently of each other H. C₁-C₂₄alkyl,     C₁-C₂₄alkyl which is substituted by E and/or Interrupted by D,     C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl,     or C₂-C₂₀heteroaryl which is substituted by E, wherein D, E, R²⁵ and     R²⁶ are defined as above.

Preferably, Y¹ is selected from

wherein R⁶ is C₁-C₂₄alkoxy, or —O—C₇-C₂₅aralkyl, R⁷ is H, or C₁-C₂₄alkyl, R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, especially C₄-C₁₂alkyl, which can be interrupted by one or two oxygen atoms, and R^(25′) is C₁-C₂₄alkyl, or C₆-C₁₀aryl.

-   Y² is preferably a single bond, —O—, —S—, —NR²⁵, a group of formula     wherein R²⁵, R⁹ and R¹⁰ are defined as above.

In a first aspect, the present Invention relates to an electroluminescent device, wherein the 2H-benzotriazole compound is a compound of formula II, especially of formula

wherein

-   A²¹, A²², A²³ and A²⁴ are independently of each other hydrogen,     halogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, C₆-C₁₈aryl, —NR²⁵R²⁶,     —CO NR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, especially a group of     formula -   A²² and A²³ or A¹¹ and A²³ are a group of formula -   A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷, and A¹⁸ are independently of each     other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, C₆-C₁₈aryl,     —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, wherein -   R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl,     C₆-C₁₈aralkyl, or C₁-C₂₄alkyl, R²⁷ is C₁-C₂₄alkyl, and -   Y³ is a group of formula     wherein -   R⁴¹ is hydrogen, C₁-C₂₄alkoxy, or OC₇-C₁₈aralkyl, -   R⁴² is hydrogen, or C₁-C₂₄alkyl, -   R⁴³ is hydrogen, halogen, —CONR²⁵R²⁶, —COOR²⁷, -    wherein -   E¹ is —S—, —O—, or —NR^(25′)—, wherein R^(25′) is C₁-C₂₄alkyl, or     C₆-C₁₀aryl, -   R¹¹⁰ is H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶,     —CONR²⁵R²⁶, or —COOR⁷, or -   R⁴² and R⁴³ are a group of formula -   R⁴⁴ is hydrogen, or C₁-C₂₄alkyl, -   R⁴⁵ is hydrogen, or C₁-C₂₄alkyl, -   A^(11′), A^(12′), A^(13′), and A^(14′) are independently of each     other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶,     —CONR²⁵R²⁶, or —COOR²⁷, -   R⁶⁸ and R⁶⁹ are independently of each other C₁-C₂₄alkyl, especially     C₄-C₁₂alkyl, especially hexyl, heptyl, 2-ethylhexyl, and octyl,     which can be interrupted by one or two oxygen atoms, R⁷⁰, R⁷¹, R⁷²,     R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁹⁰, R⁹¹, R⁹², and R⁹³ are independently of each     other H, CN, C₁-C₂₄alkyl, C₁-C₂₄aryl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio,     —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, R²⁵ and R²⁶ are independently of     each other H, C₆-C₁₈aryl, C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, and R²⁷ is     C₁-C₂₄alkyl.

Among the compounds of formula IIa the following derivatives are preferred

wherein A²³ is halogen, or C₁-C₂₄perfluoroalkyl, and R⁴³ and Y³ is defined as above, wherein the compounds of formula IIb, IIc and IId are more preferred.

In a further embodiment, those compounds of formula II, especially of formula ha are preferred, wherein R⁴¹ is different from a hydroxy group.

In this aspect, the compounds listed below are most preferred:

wherein R¹¹¹ is hydrogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, or C₆-C₁₈aryl, and A²¹, A²², A²³, A²⁴, R²⁵, R²⁶, R⁴³, and R¹¹⁰ are defined as above.

Cpd. A²¹ A²² A²³ A²⁴ R⁴¹ R⁴² R⁴³ R⁴⁴ R⁴⁵ A1 H H H H —OCH₂Ph H H —CH₃ H A2 H H H H OCH₂R H H —CH₃ H A3 H H —CO₂CH₃ H —OCH₃ -tBu H -tBu H A4 H H Cl H —OCH₃ -tBu H -tBu H A5 H H Ph H —OCH₃ -tBu H -tBu H A6 H H —N(CH₂Ph)₂ H H H H H H A7 H H Br H —OH H H ¹⁾ ¹⁾ A8 H H Br H —OCH₃ H H ¹⁾ ¹⁾ A9 H H —N(CH₂Ph)₂ H —OCH₃ H H ¹⁾ ¹⁾ A10 H H —CF₃ H —OCH₂Ph H H —CH₃ H A11 H H —CF₃ H H H —NHPh H H A12 H H —CF₃ H H H —OPh H H A13 H H F H H H —OPh H H A14 H H Cl H H H —NPh₂ H H A15 H H H H H H —N(CH₃)CH₂Ph ¹⁾ ¹⁾ A16 H H H H ¹⁾ ¹⁾ ²⁾ ¹⁾ ¹⁾ A17 Ph H H H H H —N(Et)Ph H H A18 Ph H H Ph H H —N(CH₃)Ph H H A19 H H Ph H H H —NPh₂ H H

Cpd. A²¹ A²²² R⁴¹ R⁴² R⁴³ R⁴⁴ R⁴⁵ B1 H H H H —CO₂Et H H B2 H H H H —CO₂Na H H B3 H H H H -R′ H H B4 H H H H Br H H B5 H H H H -R″ H H B6 H H H H —NCH₃Ph H H

The present 2H-benzotriazole compounds of formula lla are for instance derivatives of known hydroxyphenyl-2H-benzotriazole compounds. Known 2H-hydroxyphenyl-2H-benzotriazole compounds are commercially useful as ultraviolet light absorbers (UVA's). 2H-Benzotriazole ultraviolet light absorbers are characterized by having an ortho hydroxyphenyl-2H-benzotriazole moiety, for example as disclosed in U.S. Pat. Nos. 3,004,896; 3,055,896; 3,072,585; 3,074,910; 3,189,615; 3,218,332; 3,230,194; 4,127,586; 4,226,763; 4,275,004; 4,278,589; 4,315,848; 4,347,180; 4,383,863; 4,675,352; 4,681,905, 4,853,471; 5,268,450; 5,278,314; 5,280,124; 5,319,091; 5,410,071; 5,436,349; 5,516,914; 5,554,760; 5,563,242; 5,574,166; 5,607,987,5,977,219 and 6,166,218, the relevant parts of which are hereby incorporated by reference.

The present 2H-benzotriazoles may be obtained by simply capping the ortho hydroxy (the phenol) of known 2H-benzotriazole UV absorbers. This is achieved for example by alkylating the phenol to obtain an ortho-hydrocarbyloxyphenyl-2H-benzotriazole, for example:

The known 2H-benzotriazole UV absorbers are prepared as disclosed in the above-mentioned U.S. Patents. The benzotriazoles of this invention may have substitution patterns as disclosed in the above-mentioned U.S. Patents. The term “alkylating” above refers to “capping” the hydroxy with any suitable hydrocarbyl group. That is, the ortho hydroxy is replaced with an ortho hydrocarbyloxy group.

The term “hydrocarbyl group” broadly refers to a monovalent hydrocarbon group in which the valency is derived by abstraction of a hydrogen from a carbon atom. Hydrocarbyl includes for example aliphatics (straight and branched chain), cycloaliphatics, aromatics and mixed groups such as C₇-C₂₅aralkyl, C₇-C₂₅alkylaryl, C₂-C₂₄alkynyl, C₅-C₁₂cycloalkynyl. Hydrocarbyl Includes such groups as alkyl, C₅-C₁₂cycloalkyl, C₆-C₃₀aryl, C₇-C₂₅aralkyl, C₇-C₂₅alkylaryl, C₂-C₂₄alkenyl, and C₅-C₁₂cycloalkenyl. A hydrocarbyl may optionally be interrupted by carbonyl, carboxyl, amino, amido, thio, sulfoxide, sulfonyl and ether groups and/or may optionally be substituted by hydroxy, amino, amido, carboxyl and thio groups.

In a second aspect, the present invention relates to an EL device, comprising a 2H-benzotriazole compound of formula III, especially of formula

-   A⁴¹, A⁴², A⁴³ and A⁴⁴ are independently of each other hydrogen,     halogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, C₆-C₁₈aryl, —NR²⁵R²⁶,     —CO NR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, especially a group of     formula -   A⁴² and A⁴³ are a group of formula -   A⁵¹, A⁵², A⁵³A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹ and A⁶⁰ are independently     of each other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio,     C₆-C₁₈aryl, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl,     wherein -   E¹ is O, S, or NR²⁵, -   R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl,     C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, R²⁷ is C₁-C₂₄alkyl, and -   Y¹ is a group of formula -    wherein R⁸ is C₁-C₂₄alkoxy, or —O—C₇-C₂₅aralkyl, -   R⁷ is H, or C₁-C₂₄alkyl, -   R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, especially     C₄-C₁₂alkyl, which can be Interrupted by one or two oxygen atoms,     and -   R^(25′) is C₁-C₂₄alkyl, or C₆-C₁₀aryl.

In this aspect the compounds listed below are most preferred:

wherein Y′ is selected from

wherein R⁶ is C₁-C₂₄alkoxy, or —O—C₇-C₂₆aralkyl, R⁷ is H, or C₁-C₂₄alkyl, R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, especially C₄-C₁₂alkyl, which can be interrupted by one or two oxygen atoms, and R^(25′) is C₁-C₂₄alkyl, wherein R⁶ is C₁-C₂₄alkoxy, or —O—C₇-C₂₅aralkyl, R⁷ is H, or C₁-C₂₄alkyl, R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, especially C₄-C₁₂alkyl, which can be interrupted by one or two oxygen atoms;

In a third aspect, the present Invention relates to an EL device, comprising a 2H-benzotriazole compound of formula IV, especially of formula

-   d is 0, or 1, -   A⁴³ and A⁴⁴ are defined as above, -   Y² is a group of formula —O—, —S—, —NR²⁵—, -   a group of formula

Y³ is a group of formula

-   R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, especially     C₄-C₁₂alkyl, which can be interrupted by one or two oxygen atoms, -   R⁴¹ is C₀-C₂₄alkoxy, or C₇-C₁₅phenylalkoxy and -   R⁴⁴ is is H, C₆-C₁₀aryl, or C₁-C₂₄alkyl.

In this aspect, the following compounds are most preferred:

wherein Y³, R⁹, R¹⁰, R⁴¹ and R⁴⁴ are defined as above; and

In a fourth aspect, the present invention relates to an EL device, comprising a 2H-benzotriazole compound of formula V, wherein Ar¹, Ar², Y¹, Y², and Y^(3′) are defined as above.

In a fifth aspect, the present Invention relates to an EL device, comprising a 2H-benzotriazole compound of formula (VI), wherein Ar¹, Ar², Ar³, Y¹, Y², and Y^(3′) are defined as above.

The 2H-benzotriazoles of formulas (IV), (V) and (VI) may be prepared by any suitable process, for example, by the amination reaction as described in Hartwig et al., Journal Organic Chemistry 1999 (64), 5575, but can also be prepared by the process described below. The condensation reaction of an aromatic boronate and a bromide, commonly referred to as the “Suzuki reaction”, is tolerant of the presence of a variety of organic functional groups and as reported by N. Miyaua and A. Suzuki in Chemical Reviews, Vol. 95, pp. 457-2483 (1995).

To prepare 2H-benzotriazoles corresponding to formula (IV) 2 equivalents of a bromide of formula

are reacted with one equivalent diboronic acid or diboronate corresponding to formula

or a mixture thereof, wherein X¹¹ is independently in each occurrence a —B(OH)₂, —B(OY¹¹)₂ or

wherein Y¹¹ is independently in each occurrence a C₁-C₁alkyl group and Y¹² is Independently in each occurrence a C₂-C₁₀alkylene group, such as —CY¹³Y¹⁴—CY⁵Y⁶—, or —CY⁷Y⁸—CY⁹Y¹⁰—CY¹⁵Y¹⁶—, wherein Y⁵, Y⁶, Y⁷, Y⁸, Y⁹, Y¹⁰, Y¹³, Y¹⁴, Y¹⁵ and Y¹⁶ are independently of each other hydrogen, or a C₁-C₁₀alkyl group, especially —C(CH₃)₂C(CH₃)₂—, or —C(CH₃)₂CH₂C(CH₃)₂—, under the catalytic action of Pd and triphenylphosphine. The reaction is typically conducted at about 70° C. to 120° C. in an aromatic hydrocarbon solvent such as toluene. Other solvents such as dimethylformamide and tetrahydrofuran can also be used alone, or in mixtures with an aromatic hydrocarbon. An aqueous base, preferably sodium carbonate or bicarbonate, is used as the HBr scavenger. Depending on the reactivities of the reactants, a polymerization reaction may take 2 to 100 hours. Organic bases, such as, for example, tetraalkylammonium hydroxide, and phase transfer catalysts, such as, for example TBAB, can promote the activity of the boron (see, for example, Leadbeater & Marco; Angew. Chem. Int. Ed., 2003, 42, 1407 and references cited therein). Other variations of reaction conditions are given by T. I. Wallow and B. M. Novak in Journal of Organic Chemistry, Vol. 59, pp. 5034-5037 (1994); and M. Remmers, M. Schulze, and G. Wegner in Macromolecular Rapid Communications, Vol. 17, pp. 239-252 (1996). The 2H-benzotriazoles of formulas (IV), (V) and (VI) can be prepared accordingly.

Halogen is fluorine, chlorine, bromine and iodine.

C₁-C₂₄alkyl is a branched or unbranched radical such as for example methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, 2-ethylbutyl, n-pentyl, isopentyl, 1-methylpentyl, 1,3-dimethylbutyl, n-hexyl, 1-methylhexyl, n-heptyl, isoheptyl, 1,1,3,3-tetramethylbutyl, 1-methylheptyl, 3-methylheptyl, n-octyl, 2-ethylhexyl, 1,1,3-trimethylhexyl, 1,1,3,3-tetramethylpentyl, nonyl, decyl, undecyl, 1-methylundecyl, dodecyl, 1,1,3,3,5,5-hexamethylhexyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, icosyl or docosyl.

C₁-C₂₄perfluoroalkyl is a branched or unbranched radical such as for example —CF₃, —CF₂CF₃, —CF₂CF₂CF₃, —CF(CF₃)₂, —(CF₂)₃CF₃, and —C(CF₃)₃.

C₁-C₂₄alkoxy radicals are straight-chain or branched alkoxy radicals, e.g. methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, tert-butoxy, amyloxy, isoamyloxy or tert-amyloxy, heptyloxy, octyloxy, isooctyloxy, nonyloxy, decyloxy, undecyloxy, dodecyloxy, tetradecyloxy, pentadecyloxy, hexadecyloxy, heptadecyloxy and octadecyloxy.

C₂-C₂₄alkenyl radicals are straight-chain or branched alkenyl radicals, such as e.g. vinyl, allyl, methallyl, isopropenyl, 2-butenyl, 3-butenyl, isobutenyl, n-penta-2,4-dienyl, 3-methyl-but-2-enyl, n-oct-2-enyl, n-dodec-2-enyl, isododecenyl, n-dodec-2-enyl or n-octadec-4-enyl.

C₂₋₂₄alkynyl is straight-chain or branched and preferably C₂₋₈alkynyl, which may be unsubstituted or substituted, such as, for example, ethynyl, 1-propyn-3-yl, 1-butyn-4yl, 1-pentyn-5-yl, 2-methyl-3-butyn-2-yl, 1,4-pentadiyn-3-yl, 1,3-pentadiyn-5-yl, 1-hexyn-6-yl, cis-3-methyl-2-penten-4-yn-1-yl, trans-3-methyl-2-penten-4-yn-1-yl, 1,3-hexadlyn-5-yl, 1-octyn-8-yl, 1-nonyn-9-yl, 1-decyn-10-yl, or 1-tetracosyn-24-yl.

C₄-C₁₈cycloalkyl, especially C₅-C₁₂cycloalkyl, is preferably C₅-C₁₂cycloalkyl or said cycloalkyl substituted by one to three C₁-C₄alkyl groups, such as, for example, cyclopentyl, methyl-cyclopentyl, dimethylcyclopentyl, cyclohexyl, methylcyclohexyl, dimethylcyclohexyl, trimethyl-cyclohexyl, tert-butylcyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cyclododecyl. Cyclohexyl and cyclopentyl are most preferred.

Examples of C₄-C₁₈cycloalkyl, which is interrupted by S, O, or NR²⁵, are piperidyl, piperazinyl and morpholinyl.

C₂-C₂₄alkenyl is for example vinyl, allyl, butenyl, pentenyl, hexenyl, heptenyl, or octenyl.

Aryl is usually C₆-C₃₀aryl, preferably C₆-C₂₄aryl, which optionally can be substituted, such as, for example, phenyl, 4-methylphenyl, 4-methoxyphenyl, naphthyl, biphenylyl, 2-fluorenyl, phenanthryl, anthryl, tetracyl, pentacyl, hexacyl, terphenylyl or quadphenylyl; or phenyl substituted by one to three C₁-C₄alkyl groups, for example o-, m- or p-methylphenyl, 2,3-dimethylphenyl, 2,4-dimethylphenyl, 2,5-dimethylphenyl, 2,6-dimethylphenyl, 3,4-dimethylphenyl, 3,5-dimethylphenyl, 2-methyl-6-ethylphenyl, 4-tert-butylphenyl, 2-ethylphenyl or 2,6-diethylphenyl.

C₇-C₂₄aralkyl radicals are preferably C₇-C₁₅aralkyl radicals, which may be substituted, such as, for example, benzyl, 2-benzyl-2-propyl, β-phenethyl, α-methylbenzyl, α,α-dimethylbenzyl, ω-phenyl-butyl, ophenyl-octyl, ω-phenyl-dodecyl; or phenyl-C₁-C₄alkyl substituted on the phenyl ring by one to three C₁-C₄alkyl groups, such as, for example, 2-methylbenzyl, 3-methylbenzyl, 4-methylbenzyl, 2,4-dimethylbenzyl, 2,6-dimethylbenzyl or 4-tert-butylbenzyl or 3-methyl-5-(1′,1′,3′,3′-tetramethyl-butyl)-benzyl.

Heteroaryl is typically C₂-C₂₆heteroaryl, i.e. a ring with five to seven ring atoms or a condensed rig system, wherein nitrogen, oxygen or sulfur are the possible hetero atoms, and is typically an unsaturated heterocyclic radical with five to 30 atoms having at least six conjugated it-electrons such as thienyl, benzo[b]thienyl, dibenzo[b,d]thienyl, thianthrenyl, furyl, furfuryl, 2H-pyranyl, benzofuranyl, isobenzofuranyl, dibenzofuranyl, phenoxythienyl, pyrrolyl, imidazolyl, pyrazolyl, pyridyl, bipyridyl, triazinyl, pyrimidinyl, pyrazinyl, pyridazinyl, indolizinyl, isoindolyl, indolyl, indazolyl, purinyl, quinolizinyl, chinolyl, isochinolyl, phthalazinyl, naphthyridinyl, chinoxalinyl, chinazolinyl, cinnolinyl, pteridinyl, carbazolyl, carbolinyl, benzotriazolyl, benzoxazolyl, phenanthridinyl, acridinyl, perimidinyl, phenanthrolinyl, phenazinyl, isothiazolyl, phenothiazinyl, isoxazolyl, furazanyl or phenoxazinyl, which can be unsubstituted or substituted.

C₅-C₁₈cycloalkoxy is, for example, cyclopentyloxy, cyclohexyloxy, cycloheptyloxy or cyclooctyloxy, or said cycloalkoxy substituted by one to three C₁-C₄alkyl, for example, methylcyclopentyloxy, dimethylcyclopentyloxy, methylcyclohexyloxy, dimethylcyclohexyloxy, trimethylcyclohexyloxy, or tert-butylcyclohexyloxy.

C₈-C₂₄aryloxy is typically phenoxy or phenoxy substituted by one to three C₁-C₄alkyl groups, such as, for example o-, m- or p-methylphenoxy, 2,3-dimethylphenoxy, 2,4dimethylphenoxy, 2,5-dimethylphenoxy, 2,6-dimethylphenoxy, 3,4dimethylphenoxy, 3,5-dimethylphenoxy, 2-methyl-6-ethylphenoxy, 4-tert-butylphenoxy, 2-ethylphenoxy or 2,6-diethylphenoxy.

C₆-C₂₄aralkoxy is typically phenyl-C₁-C₉alkoxy, such as, for example, benzyloxy, α-methylbenzyloxy, α,α-dimethylbenzyloxy or 2-phenylethoxy.

C₁-C₂₄alkylthio radicals are straight-chain or branched alkylthio radicals, such as e.g. methylthio, ethylthio, propylthio, isopropylthio, n-butylthio, isobutylthio, pentylthio, isopentylthio, hexylthio, heptylthio, octylthio, decylthio, tetradecylthio, hexadecylthio or octadecylthio.

C₁-C₂₄alkylselenium and C₁-C₂₄alkyltellurium are C₁-C₂₄alkylSe- and C₁-C₂₄alkylTe-, respectively.

Examples of a five or six membered ring formed by R⁹ and R¹⁰ and R²⁵ and R²⁶, respectively are heterocycloalkanes or heterocycloalkenes having from 3 to 5 carbon atoms which can have one additional hetero atom selected from nitrogen, oxygen and sulfur, for example

which can be part of a bicyclic system, for example

Possible substituents of the above-mentioned groups are C₁-C₈alkyl, a hydroxyl group, a mercapto group, C₁-C₈alkoxy, C₁-C₈alkylthio, halogen, halo-C₁-C₈alkyl, a cyano group, an aldehyde group, a ketone group, a carboxyl group, an ester group, a carbamoyl group, an amino group, a nitro group or a silyl group.

The term “haloalkyl” means groups given by partially or wholly substituting the above-mentioned alkyl group with halogen, such as trifluoromethyl etc. The “aldehyde group, ketone group, ester group, carbamoyl group and amino group” include those substituted by an C₁-C₂₄alkyl group, a C₄-C₁₈cycloalkyl group, an C₆-C₃₀aryl group, an C₇-C₂₄aralkyl group or a heterocyclic group, wherein the alkyl group, the cycloalkyl group, the aryl group, the aralkyl group and the heterocyclic group may be unsubstituted or substituted. The term “silyl group” means a group of formula —SiR¹⁰⁵R¹⁰⁶R¹⁰⁷, wherein R¹⁰⁵, R¹⁰⁶ and R¹⁰⁷ are independently of each other a C₁-C₈alkyl group, in particular a C₁-C₄ alkyl group, a C₆-C₂₄aryl group or a C₇-C₁₂aralkyl group, such as a trimethylsilyl group.

If a substituent, such as, for example R⁶ and R⁷, occurs more than one time in a group, it can be different in each occurrence.

As described above, the aforementioned radicals may be substituted by E and/or, if desired, interrupted by D. Interruptions are of course possible only in the case of radicals containing at least 2 carbon atoms connected to one another by single bonds; C₆-C₁₈aryl is not interrupted; interrupted arylalkyl or alkylaryl contains the unit D in the alkyl moiety. C₁-C₂₄alkyl substituted by one or more E and/or interrupted by one or more units D is, for example, (CH₂CH₂O)_(n)R^(x), where n is a number from the range 1-9 and R^(x) is H or C₁-C₁₀alkyl or C₂-C₁₀alkanoyl (e.g. CO—CH(C₂H₅)C₄H₉), CH₂—CH(OR^(y′))—CH₂—O—R^(y), where R^(y) is C₁-C₂₄alkyl, C₅-C₁₂cycloalkyl, phenyl, C₇-C₁₅phenylalkyl, and R^(4′) embraces the same definitions as R^(y) or is H; C₁-C₈alkylene-COO—R^(z), e.g. CH₂COOR^(z). CH(CH₃)COOR^(z), C(CH₃)₂COOR^(z), where R^(z) is H, C₁-C₂₄alkyl, (CH₂CH₂O)₁₋₉—R^(x), and R^(x) embraces the definitions indicated above; CH₂CH₂—O—CO—CH═CH₂; CH₂CH(OH)CH₂—O—CO—C(CH₃)═CH₂.

The blue-emitting 2H-benzotriazoles of this invention emit light below about 520 nm, for example between about 380 nm and about 520 nm. For example, the blue-emitting 2H-benzotriazoles of this invention have a NTSC coordinate of about (0.14, 0.08), where the first coordinate is between about 0.12 and about 0.16, and the second coordinate is between about 0.05 and about 0.10.

The present compounds of formula I, Including those of formulae II, III, IV, V and VI, as well as the ortho-hydrocarbyloxyphenyl-2H-benzotriazoles, may also function as other than a blue-emitting organic compound, for example they may also function as a hole-injecting, hole-transporting, and electron-injecting or an electron-transporting material.

The organic EL device of the present Invention has significant industrial values since it can be adapted for a flat panel display of an on-wall television set, a flat light-emitting device, a light source for a copying machine or a printer, a light source for a liquid crystal display or counter, a display signboard and a signal light.

The material of the present invention can be used in the fields of an organic EL device, an electrophotographic photoreceptor, a photoelectric converter, a solar cell, and an Image sensor.

To obtain organic layers of this invention with the proper T_(g), or glass transition temperature, it is advantageous that the present 2H-benzotriazoles have a melting point greater than about 150° C., for example greater than about 200° C., for example greater than about 250° C., for instance greater than about 300° C.

The electroluminescent devices of the present invention are otherwise designed as is known in the art, for example as described in U.S. Pat. Nos. 5,518,824, 6,280,859, 5,629,389, 5,486,406, 5,104,740 and 5,116,708, the relevant disclosures of which are hereby incorporated by reference.

The present invention relates to an electroluminescent device having the 2H-benzotriazoles of of formula I between an anode and a cathode and emitting light by the action of electrical energy.

Typical constitutions of latest organic electroluminescent devices are:

-   (i) an anode/a hole transporting layer/an electron transporting     layer/a cathode, in which 2H-benzotriazoles of of formula I are used     either as positive-hole transport compound, which is exploited to     form the light emitting and hole transporting layers, or as electron     transport compound, which can be exploited to form the     light-emitting and electron transporting layers, -   (ii) an anode/a hole transporting layer/a light-emitting layer/an     electron transporting layer/a cathode, in which the     2H-benzotriazoles of of formula I form the light-emitting layer     regardless of whether they exhibit positive-hole or electron     transport properties in this constitution, -   (iii) an anode/a hole injection layer/a hole transporting layer/a     light-emitting layer/an electron transporting layer/a cathode, -   (iv) an anode/a hole transporting layer/a light-emitting layer/a     positive hole inhibiting layer/an electron transporting layer/a     cathode, -   (v) an anode/a hole injection layer/a hole transporting layer/a     light-emitting layer/a positive hole inhibiting layer/an electron     transporting layer/a cathode, -   (vi) an anode/a light-emitting layer/an electron transporting     layer/a cathode, -   (vii) an anode/a light-emitting layer/a positive hole inhibiting     layer/an electron transporting layer/a cathode, -   (viii) a mono-layer containing a light emitting material alone or a     combination of a light emitting material and any of the materials of     the hole transporting layer, the hole-blocking layer and/or the     electron transporting layer, and -   (ix) a multi-layered structure described in (ii) to (vii), wherein a     light emitting layer is the mono-layer defined in (viii).

The 2H-benzotriazoles of of formula I can, in principal be used for any organic layer, such as, for example, hole transporting layer, light emitting layer, or electron transporting layer, but are preferably used as the light emitting material in the light emitting layer, optionally as a host or guest component.

The light emitting compounds of this invention exhibit intense fluorescence in the solid state and have excellent electric-field-applied light emission characteristics. Further, the light emitting compounds of this invention are excellent in the injection of holes from a metal electrode and the transportation of holes; as well as being excellent in the injection of electrons from a metal electrode and the transportation of electrons. They are effectively used as light emitting materials and may be used in combination with other hole transporting materials, other electron transporting materials or other dopants.

The 2H-benzotriazoles of the present invention form uniform thin films. The light emitting layers may therefore be formed of the present 2H-benzotriazoles alone.

Alternatively, the light-emitting layer may contain a known light-emitting material, a known dopant, a known hole-injecting material or a known electron-injecting material as required. In the organic EL device, a decrease in the brightness and life caused by quenching can be prevented by forming it as a multi-layered structure. The light-emitting material, a dopant, a hole-injecting material and an electron-injecting material may be used in combination as required. Further, a dopant can improve the light emission brightness and the light emission efficiency, and can attain red, green or blue light emission. Further, each of the hole-injecting zone, the light-emitting layer and the electron-injecting zone may have the layer structure of at least two layers. In the hole-injecting zone In this case, a layer to which holes are injected from an electrode is called “hole-injecting layer”, and a layer which receives holes from the hole-injecting layer and transport the holes to a light-emitting layer is called “hole-transporting layer”. In the electron-injecting zone, a layer to which electrons are injected from an electrode is called “electron-injecting layer”, and a layer which receives electrons from the electron-injecting layer and transports the electrons to a light-emitting layer is called “electron-transporting layer”. These layers are selected and used depending upon factors such as the energy level and heat resistance of materials and adhesion to an organic layer or metal electrode.

The light-emitting material or the dopant which may be used in the light-emitting layer together with the 2H-benzotriazoles of the present invention includes for example anthracene, naphthalene, phenanthrene, pyrene, tetracene, coronene, chrysene, fluorescein, perylene, phthaloperylene, naphthaloperylene, perinone, phthaoperinone, naphthaloperinone, diphenylbutadiene, tetraphenylbutadiene, coumarine, oxadiazole, aldazine, bisbenzoxazoline, bisstyryl, pyrazine, cyclopentadiene, quinoline metal complex, aminoquinoline metal complex, benzoquinoline metal complex, imine, diphenylethylene, vinyl anthracene, diaminocarbazole, pyran, thiopyran, polymethine, merocyanine, an imidazole-chelated oxynoid compound, quinacridone, rubrene, and fluorescent dyestuffs for a dyestuff laser or for brightening.

The 2H-benzotriazoles of the present invention and the above compound or compounds that can be used in a light-emitting layer may be used in any mixing ratio for forming a light-emitting layer. That is, 2H-benzotriazoles of the present invention may provide a main component for forming a light-emitting layer, or they may be a doping material in another main material, depending upon a combination of the above compounds with the present 2H-benzotriazoles of the present invention. Good results are, for example, achieved, when DPVBi (4,4′-bis-(2,2-diphenyl-1-vinyl)biphenyl) is used as host and Compound B7 is used as guest.

Thin film type electroluminescent devices usually consist essentially of a pair of electrodes and at least one charge transporting layer in between. Usually two charge transporting layers, a hole transporting layer (next to the anode) and an electron transporting layer (next to the cathode) are present. Either one of them contains—depending on its properties as hole-transporting or electron-transporting material—an inorganic or organic fluorescence substance as light-emitting material. It is also common, that a light-emitting material is used as an additional layer between the hole-transporting and the electron-transporting layer. In the above mentioned device structure, a hole injection layer can be constructed between an anode and a hole transporting layer and/or a positive hole inhibiting layer can be constructed between a light emitting layer and an electron transporting layer to maximise hole and electron population in the light emitting layer, reaching large efficiency in charge recombination and intensive light emission.

The devices can be prepared in several ways. Usually, vacuum evaporation is used for the preparation. Preferably, the organic layers are laminated In the above order on a commercially available indium-fin-oxide (“ITO”) glass substrate held at room temperature, which works as the anode in the above constitutions. The membrane thickness is preferably in the range of 1 to 10,000 nm, more preferably 1 to 5,000 nm, more preferably 1 to 1,000 nm, more preferably 1 to 500 nm. The cathode metal, such as a Mg/Ag alloy, a binary Li—Al or LiF—Al system with an thickness in the range of 50-200 nm is laminated on the top of the organic layers. The vacuum during the deposition is preferably less than 0.1333 Pa (1×10⁻³ Torr), more preferably less than 1.333×10⁻³ Pa (1×10⁻⁵ Torr), more preferably less than 1.333×10⁻⁴ Pa (1×10⁻⁶ Torr).

As anode usual anode materials which possess high work function such as metals like gold, silver, copper, aluminum, indium, iron, zinc, tin, chromium, titanium, vanadium, cobalt, nickel, lead, manganese, tungsten and the like, metallic alloys such as magnesium/copper, magnesium/silver, magnesium/aluminum, aluminum/indium and the like, semiconductors such as Si, Ge, GaAs and the like, metallic oxides such as indium-tin-oxide (“ITO”), ZnO and the like, metallic compounds such as CuI and the like, and furthermore, electroconducting polymers, such as polyacetylene, polyaniline, polythiophene, polypyrrole, polyparaphenylene and the like, preferably ITO, most preferably ITO on glass as substrate can be used.

Of these electrode materials, metals, metallic alloys, metallic oxides and metallic compounds can be transformed into electrodes, for example, by means of the sputtering method. In the case of using a metal or a metallic alloy as a material for an electrode, the electrode can be formed also by the vacuum deposition method. In the case of using a metal or a metallic alloy as a material forming an electrode, the electrode can be formed, furthermore, by the chemical plating method (see for example, Handbook of Electrochemistry, pp 383-387, Mazuren, 1985). In the case of using an electroconducting polymer, an electrode can be made by forming it into a film by means of anodic oxidation polymerization method onto a substrate which is previously provided with an electroconducting coating. The thickness of an electrode to be formed on a substrate is not limited to a particular value, but, when the substrate is used as a light emitting plane, the thickness of the electrode is preferably within the range of from 1 nm to 300 nm, more preferably, within the range of from 5 to 200 nm so as to ensure transparency.

In a preferred embodiment ITO is used on a substrate having an ITO film thickness in the range of from 10 nm (100 Å) to 1μ (10000 Å), preferably from 20 nm (200 Å) to 500 nm (5000 Å). Generally, the sheet resistance of the ITO film is chosen in the range of not more than 100 Ω/cm², preferably not more than 50 Ω/cm².

Such anodes are commercially available from Japanese manufacturers, such as Geomatech Co.Ltd., Sanyo Vacuum Co. Ltd., Nippon Sheet Glass Co. Ltd.

As substrate either an electronconducting or electrically insulating material can be used. In case of using an electroconducting substrate, a light emitting layer or a positive hole transporting layer is directly formed thereupon, while in case of using an electrically insulating substrate, an electrode is firstly formed thereupon and then a light emitting layer or a positive hole transporting layer is superposed.

The substrate may be either transparent, semi-transparent or opaque. However, in case of using a substrate as an indicating plane, the substrate must be transparent or semi-transparent.

Transparent electrically insulating substrates are, for example, inorganic compounds such as glass, quartz and the like, organic polymeric compounds such as polyethylene, polypropylene, polymethylmethacrylate, polyacrylonitrile, polyester, polycarbonate, polyvinylchloride, polyvinylalcohol, polyvinylacetate and the like. Each of these substrates can be transformed into a transparent electroconducting substrate by providing it with an electrode according to one of the methods described above.

Examples of semi-transparent electrically insulating substrates are inorganic compounds such as alumina, YSZ (yttrium stabilized zirconia) and the like, organic polymeric compounds such as polyethylene, polypropylene, polystyrene, epoxy resins and the like. Each of these substrates can be transformed into a semi-transparent electroconducting substrate by providing it with an electrode according to one of the abovementioned methods.

Examples of opaque electroconducting substrates are metals such as aluminum, indium, iron, nickel, zinc, tin, chromium, titanium, copper, silver, gold, platinum and the like, various elctroplated metals, metallic alloys such as bronze, stainless steel and the like, semiconductors such as Si, Ge, GaAs, and the like, electroconducting polymers such as polyaniline, polythiophene, polypyrrole, polyacetylene, polyparaphenylene and the like.

A substrate can be obtained by forming one of the above listed substrate materials to a desired dimension. It is preferred that the substrate has a smooth surface. Even, if it has a rough surface, It will not cause any problem for practical use, provided that it has round unevenness having a curvature of not less than 20 μm. As for the thickness of the substrate, there is no restriction as far as it ensures sufficient mechanical strength.

As cathode usual cathode materials which possess low work function such as alkali metals, earth alkaline metals, group 13 elements, silver, and copper as well as alloys or mixtures thereof such as sodium, lithium, potassium, calcium, lithium fluoride (UF), sodium-potassium alloy, magnesium, magnesium-silver alloy, magnesium-copper alloy, magnesium-aluminum alloy, magnesium-indium alloy, aluminum, aluminum-aluminum oxide alloy, aluminum-lithium alloy, indium, calcium, and materials exemplified in EP-A 499,011 such as electroconducting polymers e.g. polypyrrole, polythiophene, polyaniline, polyacetylene etc., preferably Mg/Ag alloys, LiF—Al or Li—Al compositions can be used.

In a preferred embodiment a magnesium-silver alloy or a mixture of magnesium and silver, or a lithium-aluminum alloy, lithium fluoride-aluminum alloy or a mixture of lithium and aluminum can be used In a film thickness in the range of from 10 nm (100 Å) to 1 μm (10000 Å), preferably from 20 nm (200 Å) to 500 nm (5000 Å).

Such cathodes can be deposited on the foregoing electron transporting layer by known vacuum deposition techniques described above.

In a preferred embodiment of this invention a light-emitting layer can be used between the hole transporting layer and the electron transporting layer. Usually the light-emitting layer is prepared by forming a thin film on the hole transporting layer.

As methods for forming said thin film, there are, for example, the vacuum deposition method, the spin-coating method, the casting method, the Langmuir-Blodgett (“LB”) method and the like. Among these methods, the vacuum deposition method, the spin-coating method and the casting method are particularly preferred in view of ease of operation and cost.

In case of forming a thin film using a composition by means of the vacuum deposition method, the conditions under which the vacuum deposition is carried out are usually strongly dependent on the properties, shape and crystalline state of the compound(s). However, optimum conditions are usually as follows: temperature of the heating boat: 100 to 400° C.; substrate temperature: −100 to 350° C.; pressure: 1.33×10⁴ Pa (1×10² Torr) to 1.33×10⁻⁴ Pa (1×10⁻⁶ Torr) and deposition rate: 1 μm to 6 nm/sec.

In an organic EL element, the thickness of the light emitting layer is one of the factors determining its light emission properties. For example, if a light emitting layer is not sufficiently thick, a short circuit can occur quite easily between two electrodes sandwiching said light emitting layer, and therefor, no EL emission is obtained. On the other hand, if the light emitting layer is excessively thick, a large potential drop occurs inside the light emitting layer because of its high electrical resistance, so that the threshold voltage for EL emission increases. Accordingly, the thickness of the organic light emitting layer is limited to the range of from 5 nm to 5 μm, preferably to the range of from 10 nm to 500 nm.

In the case of forming a light emitting layer by using the spin-coating method and the casting method, ink jet printing method, the coating can be carried out using a solution prepared by dissolving the composition in a concentration of from 0.0001 to 90% by weight in an appropriate organic solvent such as benzene, toluene, xylene, tetrahydrofurane, methyltetrahydrofurane, N,N-dimethylformamide, dichloromethane, dimethylsulfoxide and the like. If the concentration exceeds 90% by weight, the solution usually is so viscous that it no longer permits forming a smooth and homogenous film. On the other hand, if the concentration is less than 0.0001% by weight, the efficiency of forming a film is too low to be economical. Accordingly, a preferred concentration of the composition is within the range of from 0.01 to 80% by weight.

In the case of using the above spin-coating or casting method, it is possible to further improve the homogeneity and mechanical strength of the resulting layer by adding a polymer binder to the solution for forming the light emitting layer. In principle, any polymer binder may be used, provided that it is soluble in the solvent in which the composition is dissolved.

Examples of such polymer binders are polycarbonate, polyvinylalcohol, polymethacrylate, polymethylmethacrylate, polyester, polyvinylacetate, epoxy resin and the like. However, ff the solid content composed of the polymer binder and the composition exceeds 99% by weight, the fluidity of the solution is usually so low that it is impossible to form a light emitting layer excellent in homogeneity. On the other hand, if the content of the composition is substantially smaller than that of the polymer binder, the electrical resistance of said layer is very large, so that it does not emit light unless a high voltage is applied thereto. Accordingly, the preferred ratio of the polymer binder to the composition is chosen within the range of from 10:1 to 1:50 by weight, and the solid content composed of both components in the solution is preferably within the range of from 0.01 to 80% by weight, and more preferably, within the range of 0.1 to 60% by weight.

As hole-transporting layers known organic hole transporting compounds such as polyvinyl carbazole

a TPD compound disclosed in J. Amer. Chem. Soc. 90 (1968) 3925:

wherein Q₁ and Q₂ each represent a hydrogen atom or a methyl group; a compound disclosed in J. Appl. Phys. 65(9) (1989) 3610:

a stilbene based compound

wherein T and T₁ stand for an organic radical; a hydrazone based compound

wherein Rx, Ry and Rz stand for an organic radical, and the like can be used.

Compounds to be used as a positive hole transporting material are not restricted to the above listed compounds. Any compound having a property of transporting positive holes can be used as a positive hole transporting material such as triazole derivatives, oxadiazole derivatives, imidazole derivatives, polyarylalkane derivatives, pyrazoline derivative, pyrazolone derivatives, phenylene diamine derivatives, arylamine derivatives, amino substituted chalcone derivatives, oxazole derivatives, stilbenylanthracene derivatives, fluorenone derivatives, hydrazone derivatives, stilbene derivatives, copolymers of aniline derivatives, PEDOT (poly(3,4-ethylenedioxy-thiophene)) and the derivatives thereof, electro-conductive oligomers, particularly thiophene oligomers, porphyrin compounds, aromatic tertiary amine compounds, stilbenyl amine compounds etc.

Particularly, aromatic tertiary amine compounds such as N,N,N′,N′-tetraphenyl-4,4′-diaminobiphenyl, N,N′-diphenyl-N,N′-bis(3-methylphenyl)-4,4′-diaminobiphenyl (TPD), 2,2′-bis(di-p-torylaminophenyl)propane, 1,1′-bis(4-di-torylaminophenyl)-4-phenylcyclohexane, bis(4-dimethylamino-2-methylphenyl)phenylmethane, bis(4-di-p-tolylaminophenyl)phenyl-methane, N,N′-diphenyl-N,N′-di(4-methoxyphenyl)-4,4′-diaminobiphenyl, N,N,N′,N′-tetraphenyl-4,4′-diaminodiphenylether, 4,4′-bis(diphenylamino)quaterphenyl, N,N,N-tri(p-tolyl)amine, 4-(di-p-tolylamino)-4′-[4-(di-p-tolylamino)stilyl]stilbene, 4-N,N-diphenylamino-(2diphenylvinyl)benzene, 3-methoxy-4′-N,N-diphenylaminostilbene, N-phenylcarbazole etc. are sed.

Furthermore, 4,4′-bis[N-(1-naphtyl)-N-phenylamino]biphenyl disclosed in U.S. Pat. No.-B-5,061,569 and the compounds disclosed in EP-A 508,562, in which three triphenylamine units are bound to a nitrogen atom, such as 4,4′,4″-tris[N-(3-methylphenyl)-N-phenylamino]triphenylamine, can be used.

A positive hole transporting layer can be formed by preparing an organic film containing at least one positive hole transporting material on the anode. The positive hole transporting layer can be formed by the vacuum deposition method, the spin-coating method, the casting method, the ink jet printing method, the LB method and the like. Of these methods, the vacuum deposition method, the spin-coating method and the casting method are particularly preferred in view of ease and cost.

In the case of using the vacuum deposition method, the conditions for deposition may be chosen in the same manner as described for the formation of a light emitting layer (see above). If it is desired to form a positive hole transporting layer comprising more than one positive hole transporting material, the coevaporation method can be employed using the desired compounds.

In the case of forming a positive hole transporting layer by the spin-coating method or the casting method, the layer can be formed under the conditions described for the formation of the light emitting layer (see above).

As in the case of forming the light emitting layer a smoother and more homogeneous positive hole transporting layer can be formed by using a solution containing a binder and at least one positive hole transporting material. The coating using such a solution can be performed in the same manner as described for the light emitting layer. Any polymer binder may be used, provided that it is soluble in the solvent in which the at least one positive hole transporting material is dissolved. Examples of appropriate polymer binders and of appropriate and preferred concentrations are given above when describing the formation of a light emitting layer.

The thickness of the positive hole transporting layer is preferably chosen In the range of from 0.5 to 1000 nm, preferably from 1 to 100 nm, more preferably from 2 to 50 nm.

As hole injection materials known organic hole transporting compounds such as metal-free phthalocyanine (H₂Pc), copper-phthalocyanine (Cu—Pc) and their derivatives as described, for example, in JP64-7635 can be used. Furthermore, some of the aromatic amines defined as hole transporting materials above, which have a lower ionisation potential than the hole transporting layer, can be used.

A hole injection layer can be formed by preparing an organic film containing at least one hole injection material between the anode layer and the hole transporting layer. The hole injection layer can be formed by the vacuum deposition method, the spin-coating method, the casting method, the LB method and the like. The thickness of the layer is preferably from 5 nm to 5 μm, and more preferably from 10 nm to 100 nm.

The electron transporting materials, which is for example a metal complex compound or a nitrogen-containing five-membered derivative, should have a high electron injection efficiency (from the cathode) and a high electron mobility. The following materials can be exemplified for electron transporting materials: lithium 8-hydroxyquinolinate, zinc bis(8-hydroxyquinolinate), copper bis(8-hydroxyquinolinate), manganese bis(8-hydroxyquinolinate), gallium tris(8-hydroxyquinolinate), tris(8-hydroxyquinolinato)-aluminum(III) and its derivatives, such as, for example, aluminum tris(2-methyl-8-hydroxyquinolinate), bis(10-hydroxybenzo[h]quinolinolato)beryllium(II) and its derivatives, zinc bis(10-hydroxybenzo[h]quinolinate), chlorogallium bis(2-methyl-8-quinolinate), gallium bis(2-methyl-8-quinolinate)(o-cresolate), aluminum bis(2-methyl-8-quinolinate)(1-naphtholate), gallium bis(2-methyl-8-quinolinate)(2-naphtholate), gallium bis(2-methyl-8-quinolinate)phenolate, zinc bis(o-(2-benzooxazolyl)phenolate), zinc bis(o-(2-benzothiazolyl)phenolate) and zinc bis(o-(2-benzotrizolyl)phenolate); oxadiazole derivatives, such as 2-(4-biphenyl)-5-(4-tert.-butylphenyl)-1,3,4-oxadiazole and 2,5-bis(1-naphthyl)-1,3,4-oxadiazole, and its dimer systems, such as 1,4-bis[2-(5-phenyloxadiazolyl)]benzene, 1,4-bis[2-(5-phenyloxadiazolyl)-4-tert-butylbenzene], 2,5-bis(1-phenyl)-1,3,4-oxadiazole, 2-(4′-tert-butylphenyl)-5-(4″-biphenyl)-1,3,4-oxadiazole, 1,3-bis(4-tert.-butylphenyl-1,3,4)oxadiazolyl)biphenylene and 1,3-bis(4-tert-butylphenyl-1,3,4-oxadiazolyl)phenylene, oxazole derivatives, dioxazole derivatives, thiazole derivatives, thiadiazole derivatives, triazole derivatives, such as 2,5-bis(1-phenyl)-1,3,4-oxazole, 1,4-bis(2-(4-methyl-5-phenyloxazolyl)benzene, 2,5-bis(1-phenyl)-1,3,4-thiazole, 2-(4′-tert-butylphenyl)-5-(4″-biphenyl)-1,3,4-thiadiazole, 2,5-bis(1-naphthyl)-1,3,4-thiadiazole, 1,4-bis[2-(5-phenylthiazolyl)]benzene, 2-(4′-tert-butylphenyl)-5-(4″-biphenyl)-1,3,4-triazole, or 2,5-bis(1-naphthyl)-1,3,4-triazole and 1,4-bis[2-(5-phenyltriazolyl)]benzene, coumarine derivatives, imidazopyridine derivatives, phenanthroline derivatives or perylene tetracarboxylic acid derivatives disclosed in Appl. Phys. Lett. 48 (2) (1986) 183.

An electron transporting layer can be formed by preparing an organic film containing at least one electron transporting material on the hole transporting layer or on the light-emitting layer.

The electron transporting layer can be formed by the vacuum deposition method, the spin-coating method, the casting method, the LB method and the like.

It is preferred that the positive hole Inhibiting materials for a positive hole Inhibiting layer have high electron injection/transporting efficiency from the electron transporting layer to the light emission layer and also have higher ionisation potential than the light emitting layer to prevent the flowing out of positive holes from the light emitting layer to avoid a drop in luminescence efficiency.

As the positive hole inhibiting material known materials, such as Balq, TAZ and phenanthroline derivatives, e.g. bathocuproine (BCP), can be used:

The positive hole inhibiting layer can be formed by preparing an organic film containing at least one positive hole inhibiting material between the electron transporting layer and the light-emitting layer. The positive hole inhibiting layer can be formed by the vacuum deposition method, the spin-coating method, the casting method, ink jet printing method, the LB method and the like. The thickness of the layer preferably is chosen within the range of from 5 nm to 2 μm, and more preferably, within the range of from 10 nm to 100 nm.

As in the case of forming a light emitting layer or a positive hole transporting layer, a smoother and more homogeneous electron transporting layer can be formed by using a solution containing a binder and at least one electron transporting material.

The thickness of an electron transporting layer is preferably chosen in the range of from 0.5 to 1000 nm, preferably from 1 to 100 nm, more preferably from 2 to 50 nm.

The hole-injecting material may be sensitivity-Increased by incorporating an electron-accepting material, and the electron-injecting material may be sensitivity-increased by incorporating an electron-donating material.

In the organic EL device of the present invention, the light-emitting layer may contain, in addition to the light-emitting 2H-benzotriazole material of the present invention, at least one of other light-emitting material, other dopant, other hole-injecting material and other electron-injecting material. For improving the organic EL device of the present invention in the stability against temperature, humidity and ambient atmosphere, a protective layer may be formed on the surface of the device, or the device as a whole may be sealed with a silicone oil, or the like.

The electrically conductive material used for the cathode is suitably selected from those having a work function of smaller than 4 eV. The electrically conductive material includes magnesium, calcium, tin, lead, titanium, yttrium, lithium, ruthenium, manganese, aluminum and alloys of these, while the electrically condutive material shall not be limited to these. Examples of the alloys include magnesium/silver, magnesium/indium and lithium/aluminum, while the alloys shall not be limited to these. Each of the anode and the cathode may have a layer structure formed of two layers or more as required.

For the effective light emission of the organic EL device, at least one of the electrodes is desirably sufficiently transparent in the light emission wavelength region of the device. Further, the substrate is desirably transparent as well. The transparent electrode is produced from the above electrically conductive material by a deposition method or a sputtering method such that a predetermined light transmittance is secured. The electrode on the light emission surface side has for instance a light-transmittance of at least 10%. The substrate is not specially limited so long as it has adequate mechanical and thermal strength and has transparency. For example, it is selected from glass substrates and substrates of transparent resins such as a polyethylene substrate, a polyethylene terephthalate substrate, a polyether sulfone substrate and a polypropylene substrate.

In the organic EL device of the present invention, each layer can be formed by any one of dry film forming methods such as a vacuum deposition method, a sputtering method, a plasma method and an ion plating method and wet film forming methods such as a spin coating method, a dipping method and a flow coating method. The thickness of each layer is not specially limited, while each layer is required to have a proper thickness. When the layer thickness is too large, inefficiently, a high voltage is required to achieve predetermined emission of light. When the layer thickness is too small, the layer is liable to have a pinhole, etc., so that sufficient light emission brightness is hard to obtain when an electric field is applied. The thickness of each layer is for example in the range of from about 5 nm to about 10 μm, for Instance about 10 nm to about 0.2 μm.

In the wet film forming method, a material for forming an intended layer is dissolved or dispersed in a proper solvent such as ethanol, chloroform, tetrahydrofuran and dioxane, and a thin film is formed from the solution or dispersion. The solvent shall not be limited to the above solvents. For improving the film formability and preventing the occurrence of pinholes in any layer, the above solution or dispersion for forming the layer may contain a proper resin and a proper additive. The resin that can be used includes insulating resins such as polystyrene, polycarbonate, polyarylate, polyester, polyamide, polyurethane, polysulfone, polymethyl methacrylate, polymethyl acrylate and cellulose, copolymers of these, photoconductive resins such as poly-N-vinylcarbozole and polysilane, and electroconducting polymers such as polythiophene and polypyrrole. The above additive Includes an antioxidant, an ultraviolet absorbent and a plasticizer.

When the light-emitting benzotriazole material of the present invention is used in a light-emitting layer of an organic EL device, an organic EL device can be improved in organic EL device characteristics such as light emission efficiency and maximum light emission brightness. Further, the organic EL device of the present invention is remarkably stable against heat and electric current and gives a usable light emission brightness at a low actuation voltage. The problematic deterioration of conventional devices can be remarkably decreased.

The 2H-benzotriazole compounds of the formula

are new and form a further subject of the present invention, wherein

-   a is 0, or 1, -   b is 0, or 1, -   X¹ is a group of formula     -   if b is 1, or Y³, if b is 0, wherein -   c is 0, or 1 -   X² and X³ are independently of each other a group of formula     -   wherein d is 0, or 1, -   Ar¹, Ar², and Ar³ are independently of each other aryl or     heteroaryl, which can optionally be substituted, especially     C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be     substituted, -   Y¹ and Y² are independently of each other a divalent linking group,     and -   Y³ and Y^(3′) are independently of each other aryl or heteroaryl,     which can optionally be substituted, especially C₆-C₃₀aryl or a     C₂-C₂₆heteroaryl, which can optionally be substituted.

Among the compounds of formula IIa the following derivatives are preferred

wherein Y³ and A²³ are defined as above, wherein the compounds of formula IIb, IIc and IId are more preferred.

The following Examples illustrate the invention. In the Examples and throughout this application, the term light emitting material means the present 2H-benzotriazole compounds.

EXAMPLE 1

2-(2-Hydroxy-5-methylphenyl)benzotriazole, 10.0 g, 44.4 mmol, potassium carbonate, 12.0 g, 86.8 mmol., acetone, 150 ml and benzyl bromide, 5.3 ml, 7.6 g, 44.6 mmol., are placed in a 500 ml flask with a stir bar. The mixture is heated to 70° C. (reflux) with vigorous stirring for a total of 8 hours. The mixture is cooled to room temperature and filtered. Removal of volatiles in vacuo give a colorless oil. The product is crystallized from 5:1 hexanes:acetone (55 ml) to give a colorless solid. Yield: 12.86 g, 40.8 mmol, 92%. T_(m)=68° C. ¹H NMR (ppm, CDCl₃): 7.97 (m, 2H), 7.53 (d, 1H), 7.42 (m, 2H), 7.24 (m, 6H), 7.04 (m, 1H), 5.14 (s, 2H), 2.35 (s, 3H). The material has a λ_(max) emission of 407 nm, CIE (0.159, 0.037) in solution.

EXAMPLE 2

2-(2-Hydroxy-5-methylphenyl)benzotriazole, 2.64 g, 11.7 mmol., potassium carbonate, 2.0 g, 14 mmol, acetone, 60 ml and 9-chloromethylanthracene, 2.66 g, 11.7 mmol., are placed in a 250 ml flask with a stir bar. The mixture is heated to 70° C. (reflux) with vigorous stirring for a total of 32 hours. The mixture is cooled to room temperature and filtered. Removal of volatiles in vacuo give a slightly yellow solid, 4.83 g, 11.6 mmol, 99%. The product is triturated in hexanes:ethyl acetate, 5:2 overnight. Filtration and removal of volatiles in vacuo give a pale yellow solid. Yield: 3.53 g, 8.50 mmol, 73%. T_(m)=132° C. ¹H NMR (ppm, CDCl₃): 8.41 (s, 1H), 8.26 (d, 2H), 7.94 (dd, 2H), 7.87 (m, 2H), 7.52 (s, 1H), 7.40 (m, 8H), 6.04 (s, 2H), 2.40 (s, 3H).

EXAMPLE 3

2,2′-Methylene bis-(6-(2H-benzotriazolyl)-4-methylphenol) (cf. U.S. Pat. No.-B-4,937,348), 3.00 g, 6.49 mmol, is slurried in DMF, 30 ml. The mixture is heated to 40° C. and NaOMe, 5.4 M in CH₃OH, 2.40 ml, 13 mmol, is added via syringe, forming an orange, homogeneous mixture. The temperature of the mixture is brought to 70° C. and benzyl bromide, 1.70 ml, 2.44 g, 14.3 mmol, is added via syringe. After 4 hours at 100° C., volatiles are removed in vacuo to give a semi-solid. The product is obtained using column chromatography, 19:1 hexanes:ethyl acetate. Yield: 3.32 g, 5.17 mmol, 80%. T_(m)=150° C. ¹H NMR (ppm, CDCl₃): 7.90 (m, 4H), 7.42 (d, 2H), 7.38 (m, 4H), 7.08 (m, 6H), 6.97 (m, 4H), 6.90 (d, 2H), 4.34 (s, 4H), 2.26 (s, 6H).

EXAMPLE 4

2-(5-carboxy-2H-benzotriazolyl)-4,6-di-tert-butylphenol, 5.00 g, 13.6 mmol., potassium carbonate, 5.64 g, 40.8 mmol, acetone, 80 ml, and DMF, 40 ml are placed in a 250 ml flask with a stir bar. Iodomethane, 4.2 ml, 9.6 g, 68 mmol, is added via syringe. The mixture is heated to 45° C. for 17 hours. Volatiles are removed in vacuo and the product is extracted with toluene. Filtration and removal of toluene in vacuo give a colorless solid in quantitative yield. 4.0 g of this material is chromatographed on silica using hexanes:ethyl acetate, 19:1, to give 3.8 g, 9.6 mmol, 95% (purification step) of product. T_(m)=112° C. ¹H NMR (ppm, CDCl₃): 8.82 (s, 1H), 8.09 (m, 2H), 7.56 (d, 1H), 7.51 (d, 1H), 4.02 (s, 3H), 3.10 (s, 3H), 1.48 (s, 9H), 1.37 (s, 9H). The material has a λ_(max) emission of 445 nm, CIE (0.157, 0.132) in solution.

EXAMPLE 5

2-(5-chloro-2H-benzotriazolyl)-4,6-di-tert-butylphenol, 30.06 g, 83.99 mmol, potassium carbonate, 23.3 g, 0.169 mol, acetone, 200 ml, and iodomethane, 26 ml, 59 g, 0.42 mol (added in portions), are heated to 45° C. for 3 days. The mixture is cooled and removed of volatiles in vacuo. The product is dissolved with toluene, filtered and removed of volatiles in vacuo to give a colorless solid. Yield, 31.18 g, 83.84 mmol., 99.8%. T_(m)=224° C. ¹H NMR (ppm, CDCl₃): 8.16 (d, 1H), 8.12 (d, 1H), 7.69 (d, 1H), 7.63 (d, 1H), 7.57 (dd, 1H), 3.25 (s, 3H), 1.62 (s, 9H), 1.51 (s, 9H).

EXAMPLE 6

The compound from example 5, 2.00 g, 5.38 mmol, potassium carbonate, 2.23 g, 16.1 mmol., and phenylboronic acid, 0.98 g, 8.04 mmol, are slurried in toluene, 30 ml, and heated to 110° C. under argon. Allyl, tricydohexylphosphinyl palladium chloride (cf. WO01/16057), 20 mg, is added, followed by heating at 110° C. for 24 hours. The mixture is cooled to room temperature and filtered through a pad of silica and washed with toluene. Volatiles are removed in vacuo and the crude material is triturated in pentane, 20 ml, for 15 hours to give a clean product. Yield, 1.53 g, 3.70 mmol, 69%. T_(m)=152° C. ¹H NMR (ppm, CDCl₃): 8.28 (s, 1H), 8.18 (d, 1H), 7.82 (m, 3H), 7.62 (m, 4H), 7.37 (m, 1H), 3.23 (s, 3H), 1.58 (s, 9H), 1.46 (s, 9H). The material has a λ_(max) emission of 413 nm, CIE (0.157, 0.053) in solution.

EXAMPLE 7

5-Amino-2-phenyl-2H-benzotriazole (Kehrmann, et. al., Chem. Ber. 1892, 25, 899.), 2.10 g, 10.0 mmol, potassium carbonate, 4.15 g, 30.0 mmole, and benzyl bromide, 3.42 g, 20.0 mmol, were placed in a 100 ml flask with DMF, 30 ml, and a stir bar. The mixture is heated to 100° C. for 15 hours. The flask is cooled and ethyl acetate is added. The solution is extracted and washed with water (5×250 ml) to remove DMF. Drying with MgSO₄, filtration and removal of volatiles in vacuo give a green-yellow semi-solid. The product is purified by trituration in hexanes:ethyl acetate, 4:1, 30 ml, followed by crystallization from toluene, 20 ml. Yield, 2.12 g, 5.43 mmol., 54%. T_(m)=158° C. ¹H NMR (ppm, CDCl₃): 8.24 (d, 2H), 7.73 (d, 1H), 7.49 (t, 2H), 7.29 (m, 1H), 7.17 (dd, 1H), 6.91 (d, 1H), 4.75 (s, 4H). The material has a λ_(max) emission of 455 nm and 497 nm in solution.

EXAMPLE 8

5-Amino-2-phenyl-2H-benzotriazole (Kehrmann, et. al., Chem. Ber. 1892, 25, 899.), 2.00 g, 9.51 mmol, potassium carbonate, 3.47 g, 25.1 mmol, and 1,2,4,5-tetrakisbromomethylbenzene, 2.14 g, 4.76 mmol, are placed in a 100 ml flask with a stir bar. DMF, 40 ml, is added and the mixture is heated to 100° C. After 4 hours, a thick yellow precipitate is found and TLC showed only one component with a very low R_(f) (1:1 hexanes:ethyl acetate). The flask is cooled and water, 30 ml, is added. The product is filtered and washed several times with water, then with methanol. Remaining volatiles are removed in vacuo to give a yellow solid. Yield, 2.49 g, 4.56 mmol, 96%. T_(m)=364° C.; T_(g)=167° C. MS (EI): 546 (M⁺).

EXAMPLE 9

a) Benzocaine, 23.00 g, 139.2 mmol, is slurried in water, 400 ml, and concentrated HCl, 29 ml, 0.35 mol, is added, forming a homogeneous solution. The mixture is cooled to 0° C. and sodium nitrite, 10.09 g, 146.2 mmol., in water, 50 ml, is added dropwise. After 40 minutes, sulfamic acid, 3.0 g, 31 mmol, in water, 20 ml, is slowly added to destroy excess nitrite. The diazonium salt is cannulated into a 2.5 l reactor containing 1-naphthylamine-2-sulfonic acid, 31.08 g, 139.2 mmol, sodium carbonate, 29.5 g, 0.278 mol, in water, 800 ml at 0° C. After 2 hours at 0 to 5° C., the product is filtered and washed with water (2×300 ml) to form a red solid. TLC shows one major spot and a minor impurity. All was used for b).

b) The product from a) and copper(II) acetate, 0.25 g, 1.38 mmol, are slurried in tert-amyl alcohol. Upon heating to 80° C., the mixture become homogeneous and tert-butyl hydroperoxide, 100 ml, 70 g, 0.78 mol, is added over 2 days. The mixture is cooled and filtered to remove the product. Washing with tert-amyl alcohol and removal of volatiles in vacuo give a pink solid. Yield, 27.46 g, 86.53 mmol, 62%. T_(m)=161° C. ¹H NMR (ppm, CDCl₃): 8.42 (d, 1H), 8.23 (d, 2H), 8.01 (d, 2H), 7.66 (d, 1H), 7.55 (m, 2H), 7.45 (m, 2H), 4.21 q, 2H), 1.22 (t, 3H).

EXAMPLE 10

The product from example 9 is slurried in ethanol:water, 1:1, 700 ml, and sodium hydroxide, 6.94 g, 0.174 mol, is added. The mixture is heated to reflux (105° C. external) for 4 hours. The flask is cooled to 70° C. and filtered to give a light brown solution of the product. Upon cooling to room temperature overnight, crystals form. The product is filtered, washed with ethanol:water, 1:1, 50 ml, and dried using high vacuum. This material is used for example 11 without purification. Yield: 21.22 g, 68.17 mmol., 79%.

EXAMPLE 11

The product from example 10, 3.00 g, 9.64 mmol, is slurried at room temperature in dichloromethane, 40 ml, containing a few drops of DMF. Thionyl chloride, 2.4 ml, 3.9 g, 33 mmol, is added via syringe, causing a precipitate to form along with an exotherm. The flask is heated to an external temperature of 53° C. for 5 hours, followed by cooling to room temperature. Volatiles are removed In vacuo to give a pale brown solid. A solution of N-phenyl-1,2-phenylenediamine, 1.78 g, 9.66 mol., in N-methylpyrrolidinone, 20 ml, is added dropwise to the solid under argon. After 30 minutes at room temperature, the mixture is heated to 60° C. for 2 hours. The product is isolated by pouring into water, filtration and washing with water as well as methanol, 25 ml. High vacuum is used to isolate the material. The material is heated to 260° C. under vacuum (100 mbar) for 3 hours to form a melt of the product. After cooling to room temperature, the product is extracted with dichloromethane and filtered through a silica pad. Solvent is removed in vacuo to give a near colorless solid that is one spot by TLC (hexanes:ethyl acetate, 1:1). Yield, 3.03 g, 6.93 mmol, 72%. The material is purified by trituration in MeOH, 25 ml, overnight. Filtration and removal of volatiles in vacuo give a colorless solid. Yield, 2.48 g, 5.67 mmol, 59%. T_(m)=208° C., T_(g)=75° C. MS (EI): 437 (M⁺). ¹H NMR (ppm, CDCl₃): 8.54 (d, 1H), 8.27 (d, 2H), 7.84 (m, 2H), 7.71 (m, 2H), 7.67 (d, 1H), 7.58 (m, 3H), 7.46 (m, 3H), 7.32 (m, 3H), 7.23 (m, 2H).

EXAMPLE 12

3,7-Diaminodibenzofuran (Nimura, S., et. al. J. Phys. Chem. A 1997, 101, 2083.), 10.0 g, 50.4 mmol., water, 150 ml, and concentrated HCl, 25 ml, 0.30 mol., are placed in a 500 ml reactor. Sodium nitrite, 7.00 g, 0.101 mol. in water, 28 ml, is added dropwise at 0° C. DMF, 45 ml, is added slow enough to not let the temperature above SIC. After 10 minutes, the diazonium salt is added dropwise to a solution of 2-naphthylamine, 14.4 g, 0.101 mol. in water, 100 ml, DMF, 50 ml, and HCl, 10 ml, 0.12 mol, to give a dark mixture. Sodium acetate trihydrate, 40 g, 0.29 mol., is added to the reaction at 0° C., followed by stirring for 2 hours at room temperature. The bis-azo intermediate is filtered and washed with water.

The product is placed in a 1 l reactor with pyridine, 225 ml, and copper(II) acetate monohydrate, 50 g, 0.25 mol. The mixture is heated to reflux for 6 hours and then cooled to room temperature. The beige product is filtered and washed with water, 7×150 ml, and methanol, 2×50 ml. Volatiles are removed in vacuo. The compound is purified by dissolving in hot trichlorobenzene, filtering through activated carbon (while hot) and cooling to room temperature to give yellow crystals. Yield, 13.15 g, 26.2 mmol., 52%. T_(m)=348° C. MS (EI): 502 (M⁺).

EXAMPLE 13

a) 2,5-dibromoaniline, 19.71 g, 78.5 mmol, is dissolved in EtOH, 130 ml, at room temperature. While stirring, H₂SO₄, 4.2 ml, 7.7 g, 79 mmol, is added via syringe, causing a precipitate to form. Volatiles are removed in vacuo to give a beige powder.

The anilinium sulfate salt above, 26.00 g, 77.0 mmol, is slurried in water, 200 ml, and HCl, 5 ml, 60 mmol, at 0° C. Sodium nitrite, 5.31 g, 77.0 mmol, in water, 30 ml, is added dropwise.

The reaction is stirred for 2 hours at 0° C. The diazonium salt solution is added portion-wise to a solution of 2-naphthol, 11.1 g, 77.0 mmol, in ethanol, 450 ml, also at 0° C. The orange mixture is stirred for 3 hours and warmed to room temperature. The product is filtered and washed with water (3×200 ml) and dried under vacuum. The product is purified by trituration in 19:1 hexanes:ethyl acetate (200 ml), filtered and dried in vacuo to give an orange solid. Yield, 28.13 g, 69.27 mmol, 90%. T_(dec)=170° C. ¹H NMR (ppm, CDCl₃): 8.63 (d, 1H), 8.32 (d, 1H), 7.85 (d, 1H), 7.72 (m, 2H), 7.62 (d, 1H), 7.57 (t, 1H), 7.35 (dd, 1H), 6.93 (d, 1H).

b) The product from a), 28.13 g, 69.27 mmol, sodium azide, 4.50 g, 69.3 mmol, and copper(1) bromide, 0.10 g, 0.69 mmol, are placed in a 500 ml flask with a stir bar and DMF, 200 ml. The mixture is heated to 80° C. for 2 hours and cooled to room temperature. The solution Is poured into water, 500 ml, and washed with water (4×500 ml). Removal of volatiles in vacuo give a brown solid, pure by TLC (1:1 hexanes:ethyl acetate). Yield, 21.1 g, 62.0 mmol, 90%. ¹H NMR (ppm, CDCl₃): 8.62 (d, 1H), 8.22 (s, 1H), 7.90 (m, 3H), 7.60 (m, 2H), 7.41 (m, 2H).

EXAMPLE 14

The product from example 13, 20.7 g, 60.9 mmol, and potassium carbonate, 16.9 g, 122 mmol, are placed in a 500 ml flask with a stir bar and DMF, 200 ml. Iodomethane, 7.8 ml, 17.8 g, 122 mmol, is added via syringe. The flask is heated to 50° C. (external) for 3 hours. Volatiles are removed in vacuo and the product is extracted with toluene:water (1:1, 11). The organic phase is separated and dried. Filtration and removal of volatiles in vacuo give a brown solid, pure by TLC and NMR. Yield, 17.2 g, 48.6 mmol, 80%. T_(m)=116° C. ¹H NMR (ppm, CDCl₃): 8.22 (s, 1H), 8.06 (d, 1H), 7.92 (d, 1H), 7.87 (m, 1H), 7.56 (dd, 1H), 7.41 (m, 3H), 6.92 (m, 1H), 3.88 (s, 3H).

EXAMPLE 15

The product from example 14, 5.00 g, 14.1 mmol, diphenylamine, 2.39 g, 14.1 mmol, sodium tert-butoxide, 2.71 g, 28.2 mmol, tris-(dibenzylidineacetone) dipalladium(0), 129 mg, 0.141 mmol, and bis-(diphenylphosphino) ferrocene, 156 mg, 0.281 mmol, are placed in a 250 ml flask with a stir bar. Toluene, 100 ml, is added and the mixture is heated to 100° C. for 24 hours. The product is adsorbed onto alumina and chromatographed using hexanes:ethyl acetate (15:1). The product is further purified via sublimation. T_(m)=214° C., T_(g)=78° C. MS (EI): 442 (M⁺). ¹H NMR (ppm, CDCl₃): 8.14 (d, 1H), 7.94 (d, 2H), 7.51 (m, 4H), 7.38 (m, 5H), 7.28 (m, 4H), 7.16 (m, 3H), 4.00 (s, 3H). The material has a λ_(max) emission of 478 nm in solution.

EXAMPLE 16

3-Aminofluoranthene, 10.85 g, 49.94 mmol, is suspended in water, 50 ml, and HCl, 12 M, 10 ml, 0.12 mol, at 0° C. Sodium nitrite, 3.50 g, 50.7 mmol, In water, 10 ml, is added dropwise over 15 minutes. After 30 minutes at 0° C., the red-brown solution is filtered. Tobias acid (2-naphthylamine-1-sulfonic acid), 11.15 g, 49.96 mmol, is dissolved in pyridine, 50 ml, and cooled to 0° C. The diazonium salt solution is then added dropwise over 30 minutes at 0° C. After 2 hours, the suspension is filtered, washed with water and dried in vacuo to give a purple-red solid.

The material, 15.6 g, 42.0 mmol, is heated in pyridine, 250 ml, to 60° C. in a 1 l reactor. Copper(II) sulfate pentahydrate, 26.4 g, 0.105 mol, in water, 100 ml, is added dropwise to the azo compound. The temperature is then raised to 90° C. for 4 hours. The mixture is cooled to room temperature and filtered to give a pale brown solid. The compound is purified by crystallization. Yield, 7.9 g, 21.4 mmol, 51%. T_(m)=155° C. MS (APCI): 370.1 (M+1). The material has a λ_(max) emission of 478 nm in solution.

EXAMPLE 17

a) 4-Bromoaniline, 23.63 g, 137.4 mmol, is dissolved in water, 250 ml, using HCl, 31 ml, 372 mmol. The mixture i cooled to 0° C. and sodium nitrite, 9.48 g, 137 mmol, in water, 30 ml, is dded dropwise over 30 minutes. After 45 minutes, the diazonium salt is added via cannula to a mixture of Tobias acid, 30.66 g, 137.4 mmol, and sodium carbonate, 25.1 g, 234 mmol, in water, 600 ml, at 0° C. After 2 hours, the red precipitate is filtered and washed with water (2×300 ml). The product is dried in vacuo to give a red solid. The compound is triturated in methanol, 175 ml, overnight. Filtration and removal of volatiles in vacuo give a red solid, pure by TLC. The red dye is used directly for the next step. MS (EI): 325 (M+). ¹H NMR (ppm, CDCl₃): 8.74 (d, 1H), 7.68 (d, 2H), 7.59 (d, 2H), 7.53 (m, 2H), 7.47 (t, 1H), 7.27 (t, 1H), 6.77 (d, 1H).

b) The product from a), 10.00 g, 30.66 mmol, and copper(II) acetate, 50 mg, 0.28 mmol, are placed in a 250 ml flask with a stir bar. tert-Amyl alcohol, 100 ml, is added and the mixture is heated to 80° C. tert-Butyl hydroperoxide, 13.7 ml, 100 mmol, is slowly added and the reaction is monitored by TLC. The flask is cooled to room temperature and the product is filtered. Washing with tert-amyl alcohol and removal of volatiles in vacuo give a pale rose solid. Yield, 7.82 g, 24.1 mmol, 79%. MS (EI): 323 (M+). ¹H NMR (ppm, CDCl₃): 8.49 (d, 1H), 8.15 (d, 2H), 7.76 (d, 1H), 7.64 (m, 2H), 7.55 (m, 4H).

EXAMPLE 18

a) Magnesium turnings, 1.67 g, 68.7 mmol, are dry stirred under argon for one hour. Ether, 32 ml, is added, followed by 2 drops of dibromoethane. 4-Bromo-4′-tert-butylbiphenyl (Murphy, S., et. al. J. Org. Chem. 1995, 60, 2411.) 10.0 g, 34.6 mmol, in ether, 20 ml, and THF, 25 ml, is added dropwise over 1 hour. The mixture is refluxed for 2 hours at 37° C. In a separate flask, triisopropylborate, 9.4 ml, 7.7 g, 41 mmol, and THF, 30 ml, are cooled to −78° C. under argon. The above Grignard reagent is added via cannula and the reaction is allowed to stir at −78° C. for 1 hour. The flask is warmed to room temperature and stirred for an additional hour. The mixture is poured into a flask containing HCl, water and is stirred for 2 hours. The beige product is filtered and washed with water. Removal of volatiles in vacuo give an off-white solid. Yield, 5.67 g, 22.3 mmol, 64%. T_(m)=192° C. ¹H NMR (ppm, (CD₃)₂SO): 7.80 (d, 2H), 7.55 (two overlapping doublets, 4H), 7.41 (d, 2H), 1.25 (s, 9H).

b) The product from a), 2.00 g, 6.13 mmol, the product from example 19, 2.54 g, 9.99 mmol, potassium carbonate, 2.36 g, 17.1 mmol, and toluene, 50 ml, are stirred under argon for 30 minutes. Allyl, tricyclohexylphosphinyl palladium chloride (WO01116057), 40 mg, is added, followed by heating at 110° C. for 24 hours. The mixture is cooled to room temperature and adsorbed onto silica gel. The product is purified by column chromatography using hexanes:ethyl acetate, 9:1, to give a tan solid, 0.90 g, 1.98 mmol, 32%. T_(m)=245° C. The product has a λ_(max) emission of 414 nm in solution, with a quantum efficiency of 70%.

APPLICATION EXAMPLE 1 Device

The following device structure is prepared:

-   ITO (anode, ITO is indium tin oxide) -   CuPC (copper phthalocyanine; hole Injection material) -   NPD (4,4′-bis-(1-naphthyl-phenylamino)biphenyl; hole transporting     material) -   DPVBi (4,4′-bis-(2,2-diphenyl-1-vinyl)biphenyl) (host)/Compound of     example 16 (2.6%, guest) -   Alq3 (tris-8-quinolinato aluminum; electron transporting material) -   LiF/AI (cathode).

Using this device structure, a maximum brightness of 816 cd/m² was observed at 9V (0.89 cd/A) with an emission λ_(max) at 489 nm, similar to the guest material in solution.

APPLICATION EXAMPLE 2 Device

The following device structure is prepared:

-   ITO (anode, ITO is indium tin oxide) -   CuPC (copper phthalocyanine; hole Injection material) -   NPD (4,4′-bis-(1-naphthyl-phenylamino)biphenyl; hole transporting     material) -   DPVBi (4,4′-bis-(2,2-diphenyl-1-vinyl)biphenyl) (host)/Compound of     example 15 (2.2%, guest) -   Alq3 (tris-8-quinolinato aluminum; electron transporting material) -   LiF/Al (cathode).

Using this device structure, a maximum brightness of 3120 cd/m² was observed at 11V (1.8 cd/A) with an emission 4 at 493 nm, similar to the guest material in solution.

APPLICATION EXAMPLE 3 Device

The following device structure is prepared:

-   ITO (anode, ITO is indium tin oxide) -   CuPC (copper phthalocyanine; hole injection material) -   NPD (4,4′-bis-(1-naphthyl-phenylamino)biphenyl; hole transporting     material) Compound of example 12 -   Alq3 (tris-8-quinolinato aluminum; electron transporting material) -   LiF/Al (cathode).

Using this device structure, a maximum brightness of 1230 cd/M² was observed at 15V (1.1 cd/A) with an emission λ_(max) at 471 nm.

APPLICATION EXAMPLE 4 Device

The following device structure is prepared:

-   ITO (anode, ITO is Indium tin oxide) -   CuPC (copper phthalocyanine; hole injection material) -   NPD (4,4′-bis-(1-naphthyl-phenylamino)biphenyl; hole transporting     material) Compound of example 11 -   Alq3 (tris-8-quinolinato aluminum; electron transporting material) -   LiF/Al (cathode).

Using this device structure, a maximum brightness of 720 cd/M² was observed at 10V (0.71 cd/A) with an emission at 432 nm.

APPLICATION EXAMPLE 5 Device

The following device structure is prepared:

-   ITO (anode, ITO is indium fin oxide) -   CuPC (copper phthalocyanine; hole injection material) -   NPD (4,4′-bis-(1-naphthyl-phenylamino)biphenyl; hole transporting     material) -   DPVBi (4,4-bis-(2,2-diphenyl-1-vinyl)biphenyl) (host)/Compound of     example 7 (3.1%, guest) -   Alq3 (tris-8-quinolinato aluminum; electron transporting material) -   LiF/Al (cathode).

Using this device structure, a maximum brightness of 4130 cd/M² was observed at 14V (2.1 cd/A) with an emission λ_(max) at 461 nm, similar to the guest material in solution.

The organic EL device obtained in the Example of the present invention show an excellent light emission brightness and achieved a high light emission efficiency. When the organic EL devices obtained in the above Examples are allowed to continuously emit light at 3 (mA/cm²), all the organic EL devices remain stable. Since the light-emitting materials of the present invention have a very high fluorescence quantum efficiency, the organic EL devices using the light-emitting materials achieved light emission with a high brightness in a low electric current applied region, and when the light-emitting layer additionally uses a doping material, the organic EL devices are improved in maximum light emission brightness and maximum light emission efficiency. Further, by adding a doping material having a different fluorescent color to the light-emitting material of the present invention, there are obtained light-emitting devices having a different light emission color.

The organic EL devices of the present invention accomplish improvements in light emission efficiency and light emission brightness and a longer device life, and does not impose any limitations on a light-emitting material, a dopant, a hole-injecting material, an electron-injecting material, a sensitizer, a resin and an electrode material used in combination and the method of producing the device.

The organic EL device using the material of the present invention as a light-emitting material achieves light emission having a high brightness with a high light emission efficiency and a longer life as compared with conventional devices. According to the light-emitting material of the present invention and the organic EL device of the present invention, there can be achieved an organic EL device having a high brightness, a high light emission efficiency and a long life. 

1. An electroluminescent device, comprising a 2H-benzotriazole compound, compound of the formula

where a is 0, or 1, b is 0, or 1, X¹ is a group of formula

if b is 1, or Y³, if b is 0, wherein c is 0, or 1 X² and X³ are independently of each other a group of formula

wherein d is 0, or 1, Ar¹, Ar², and Ar³ are independently of each other C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted, Y¹ and Y² are independently of each other a divalent linking group, and Y³ and Y³ are independently of each other aryl or heteroaryl, which can optionally be C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted.
 2. An electroluminescent device according to claim 1, comprising a 2H-benzotriazole compound of the formula

d, Ar¹, Ar², Ar³, Y¹ and Y² are defined as in claim 1, Ar⁴ stand for C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted, and Y³ and Y^(3′) are independently of each other C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted.
 3. An electroluminescent device according to claim 2, wherein

in formula II or III are independently of each other a group of formula

wherein A²¹, A²², A²³, A²⁴, A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷ and A¹⁸ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, —NR²⁵R²⁶, C₁-C₂₄alkylthio, —PR³², R³², C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, or A²² and A²³ or A¹¹ and A²³ are a group

 two groups A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷ and A¹⁸, which are neighbouring to each other, are a group

 wherein A³¹, A³², A³³, A³⁴, A³⁵, A³⁶ and A³⁷ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, D is —CO—; —COO—; —S—; —SO—; —SO₂—; —O—; —NR²⁵; —SiR³⁰R³¹—; —POR³²—; —CR²³═CR²⁴; or —C≡C—; and E is —OR²⁹; —SR²⁹; —NR²⁵R²⁶; —COR²⁸; —COOR²⁷; —CONR²⁵R²⁶; —CN; —OCOOR²⁷; or halogen; wherein R²³, R²⁴, R²⁵ and R²⁶ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—; or R²⁵ and R²⁶ together form a five or six membered ring, R²⁷ and R²⁸ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R²⁹ is H; C₆-C₁₈aryl; C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R³⁰ and R³¹ are independently of each other C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, and R³² is C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl.
 4. An electroluminescent device according to claim 2, wherein

in formula IV are independently of each other a group of formula

wherein A⁴¹, A⁴², A⁴³, A⁴⁴, A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷A⁵⁸, A⁵⁹ and A⁶⁰ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, NR²⁵R²⁶, C₁-C₂₄alkylthio, —PR³²R³², C₅-C₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, or A⁴² and A⁴³ or A⁴² and A⁵¹ are a group

 two groups A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹ and A⁶⁰, which are neighbouring to each other, are a group

wherein A⁶¹, A⁶², A⁶³, A⁶⁴, A⁶⁵, A⁶⁶, A⁶⁷, A⁶⁸, A⁶⁹ and A⁷⁰ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁶, D is —CO—; —COO—; —S—; —SO—; —SO₂—; —O—; —NR²⁵—; —SiR³⁰R³¹—; —POR³²—; —CR²³═CR²⁴—; or —C≡C—; and E is —OR²⁹; —SR²⁹; —NR²⁵R²⁶; —COR²⁸; —COOR²⁷; —CONR²⁵R²⁶; —CN; —OCOOR²⁷; or halogen; wherein R²³, R²⁴, R²⁵ and R²⁶ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—; or R²⁵ and R²⁶ together form a five or six membered ring, R²⁷ and R²⁸ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R²⁹ is H; C₆-C₁₈aryl; C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R³⁰ and R³¹ are independently of each other C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, and R³² is C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, wherein one of the substituents A⁴¹, A⁴², A⁴³, A⁴⁴, A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹, A⁶⁰, A⁶¹, A⁶², A⁶³, A⁶⁴, A⁶⁵, A⁶⁶, A⁶⁷, A⁶⁸, A⁶⁹ and A⁷⁰ represents a single bond.
 5. An electroluminescent device according to claim 2, wherein Y³ and Y³ are independently of each other a group of formula

R⁴¹, R⁴², R⁴³, R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹, R⁵², R⁵³, R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, R⁶¹, R⁶², R⁶³, R⁶⁴, R⁶⁵, R⁶⁶, R⁶⁷, R⁷⁰, R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁷⁷, R⁸⁰, R⁸¹, R⁸², R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, and R⁸⁷ are independently of each other H, C₁-C₂₄alkyl, which is optionally substituted by E and/or interrupted by D, C₁-C₂₄alkenyl, which is optionally substituted by E, C₅-C₁₂cycloalkyl, which is optionally substituted by E, C₅-C₁₂cycloalkoxy, which is optionally substituted by E, C₆-C₁₈aryl, which is optionally substituted by E, C₁-C₂₄alkoxy, which is optionally substituted by E and/or interrupted by D, C₆-C₁₈aryloxy, which is optionally substituted by E, C₇-C₁₈arylalkoxy, which is optionally substituted by E, C₁-C₂₄alkylthio, which is optionally substituted by E and/or interrupted by D, C₁-C₂₄alkylselenium, which is optionally substituted by E and/or interrupted by D, C₁-C₂₄alkyltellurium, which is optionally substituted by E and/or interrupted by D, C₂-C₂₀heteroaryl which is substituted by E, or C₆-C₁₈aralkyl, which is optionally substituted by E, or two groups R⁴¹, R⁴², R⁴³, R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹, R⁵², R⁵³, R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, R⁶¹, R⁶², R⁶³, R⁶⁴, R⁶⁵, R⁶⁶, R⁶⁷, R⁷⁰, R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁷⁷, R⁷⁸, R⁸⁰, R⁸², R⁸¹, R⁸², R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, and R⁸⁷, which are neighbouring to each other, are a group

wherein A⁹⁰, A⁹¹, A⁹², A⁹³, A⁹⁴, A⁹⁵, A⁹⁶ and A⁹⁷ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, R⁶⁸, R⁶⁹, R⁷⁸, R⁷⁹, R⁸⁸ and R⁸⁹ are independently of each other C₁-C₁₈ alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, or R⁶⁸ and R⁶⁹, R⁷⁸ and R⁷⁹, and/or R⁸⁸ and R⁸⁹ form five- or six-membered ring, or R⁶⁸ and R⁷⁰, R⁶⁹ and R⁷³, R⁷⁷ and R⁷⁸ and/or R⁸⁴ and R⁸⁹ are a group

D is —CO—; —COO—; —S—; —SO—; —SO₂—; —O—; —NR²⁵—; —SiR³⁰R³¹—; —POR³²—; —CR²³═CR²⁴—; or —C≡C—; and E is —OR²⁹; —SR²⁹; —NR²⁵R²⁶; —COR²⁸; —COOR²⁷; —CONR²⁵R²⁶; —CN; —OCOOR²⁷; or halogen; wherein R²³, R²⁴, R²⁵ and R²⁶ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—; or R²⁵ and R²⁶ together form a five or six membered ring, in particular R²⁷ and R²⁸ are independently of each other H; C₆-C₁₈aryl; C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R²⁹ is H; C₆-C₁₈aryl; C₆-C₁₋₈aryl, which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy; C₁-C₂₄alkyl; or C₁-C₂₄alkyl which is interrupted by —O—, R³⁰ and R³¹ are independently of each other C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, and R³² is C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl.
 6. An electroluminescent device according to claim 1, wherein Y¹ and Y² are independently of each other

n1, n2, n3, n4, n5, n6 and n7 are 1, 2, or 3, E¹ is —S—, —O—, or —NR^(25′)—, wherein R^(25′) is C₁-C₂₄alkyl, or C₆-C₁₀aryl, R⁶ and R⁷ are independently of each other H, halogen, hydroxy, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₁-C₂₄perfluoroalkyl, C₅-C₁₂cycloalkyl, C₅-C₁₂cycloalkyl which is substituted by E and/or interrupted by S—, —O—, or —NR²⁵—, C₅-C₁₂cycloalkoxy, C₅-C₁₂cycloalkoxy which is substituted by E, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, C₇-C₂₅aralkyl, C₇-C₂₅aralkyl, which is substituted by E, C₇-C₂₅aralkoxy, C₇-C₂₅aralkoxy which is substituted by E, or —CO—R²⁸, R⁸ is C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄ aryl, or C₇-C₂₅aralkyl, R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, C₂-C₂₀heteroaryl which is substituted by E, C₂-C₂₄alkenyl, C₂-C₂₄alkynyl, C₁-C₂₄alkoxy, C₁-C₂₄alkoxy which is substituted by E and/or interrupted by D, or C₇-C₂₅aralkyl, or R⁹ and R¹⁰ form a five- or six-membered ring, R¹⁴ and R¹⁵ are independently of each other H, C₁-C₂₄alkyl, C₁-C₂₄alkyl which is substituted by E and/or interrupted by D, C₆-C₂₄aryl, C₆-C₂₄aryl which is substituted by E, C₂-C₂₀heteroaryl, or C₂-C₂₀heteroaryl which is substituted by E, D is —CO—, —COO—, —S—, —SO—, —SO₂—, —O—, —NR²⁵, —SiR³⁰R³¹—, POR³², CR²³═CR²⁴, or —C≡C—, and E is —OR²⁹, —SR²⁵, —NR²⁵R²⁶, —COR²⁸, —COOR²⁷, —CONR²⁵R²⁶, —CN, —OCOOR²⁷, or halogen, wherein R²³, R²⁴, R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkyl, or C₁-C₂₄alkyl which is interrupted by —O—, or R²⁵ and R²⁶ together form a five or six membered ring, R²⁷ and R²⁸ are independently of each other H, C₆-C₁₈aryl, C₆-C₁₈aryl which is substituted by C₁-C₂₄alkyl, or C₁-C₂₄alkoxy, C₁-C₂₄alkyl, or C₁-C₂₄alkyl which is interrupted by —O—, R²⁹ is H, C₆-C₁₈aryl, C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkyl, or C₁-C₂₄alkyl which is interrupted by —O—, R³⁰ and R³¹ are independently of each other C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl, and R³² is C₁-C₂₄alkyl, C₆-C₁₈aryl, or C₆-C₁₈aryl, which is substituted by C₁-C₂₄alkyl.
 7. An electroluminescent device according to claim 2, wherein the 2H-benzotriazole compound is a compound of formula

A²¹, A²², A²³ and A²⁴ are independently of each other hydrogen, halogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, C₆-C₁₈aryl, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, A²² and A²³ or A¹¹ and A²³ are a group of formula

A¹¹, A¹², A¹³, A¹⁴, A¹⁵, A¹⁶, A¹⁷, and A¹⁸ are independently of each other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, C₆-C₁₈aryl, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, wherein R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl, C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, R²⁷ is C₁-C₂₄alkyl, and Y³ is a group of formula

R⁴¹ is hydrogen, C₁-C₂₄alkoxy, or OC₇-C₁₈aralkyl, R⁴² is hydrogen, or C₁-C₂₄alkyl, R⁴³ is hydrogen, halogen, —CONR²⁵R²⁶, —COOR²⁷,

E¹ is —S—, —O—, or —NR^(25′)—, wherein R^(25′) is C₁-C₂₄alkyl, or C₆-C₁₀aryl, R¹¹⁰ is H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or R⁴² and R⁴³ are a group of formula

R⁴⁴ is hydrogen, or C₁-C₂₄alkyl, R⁴⁵ is hydrogen, or C₁-C₂₄alkyl, A^(11′), A^(12′), A^(13′), and A^(14′) are independently of each other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, R⁶⁸ and R⁶⁹ are independently of each other C₁-C₂₄alkyl, which can be interrupted by one or two oxygen atoms, R⁷⁰, R⁷¹, R⁷², R⁷³, R⁷⁴, R⁷⁵, R⁷⁶, R⁹⁰, R⁹¹, R⁹², and R⁹³ are independently of each other H, CN, C₁-C₂₄alkyl, C₆-C₁₀aryl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl, C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, and R²⁷ is C₁-C₂₄alkyl.
 8. An electroluminescent device according to claim 2, wherein the 2H-benzotriazole compound is a compound of formula

A⁴¹, A⁴², A⁴³ and A⁴⁴ are independently of each other hydrogen, halogen, C₁-C₂₄alkyl, C₁-C₂₄perfluoroalkyl, C₆-C₁₈aryl, —NR²⁵R²⁶, —CO NR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, A⁴² and A⁴³ are a group of formula

A⁵¹, A⁵², A⁵³, A⁵⁴, A⁵⁵, A⁵⁶, A⁵⁷, A⁵⁸, A⁵⁹ and A⁶⁰ are independently of each other H, CN, C₁-C₂₄alkyl, C₁-C₂₄alkoxy, C₁-C₂₄alkylthio, C₆-C₁₈aryl, —NR²⁵R²⁶, —CONR²⁵R²⁶, or —COOR²⁷, or C₂-C₁₀heteroaryl, wherein E¹ is O, S, or —NR^(25′)—, R²⁵ and R²⁶ are independently of each other H, C₆-C₁₈aryl, C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, R²⁷ is C₁-C₂₄alkyl, and Y¹ is a group of formula

R⁶ is C₁-C₂₄alkoxy, or —O—C₇-C₂₅aralkyl, R⁷ is H, or C₁-C₂₄alkyl, R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, which can be interrupted by one or two oxygen atoms, and R^(25′) is C₁-C₂₄alkyl, or C₆-C₁₀aryl.
 9. An electroluminescent device according to claim 2, wherein the 2H-benzotriazole compound is a compound of formula

(VIa), wherein d is 0, or 1, Y² is a group of formula —O—, —S—, —NR²⁵—,

Y³ is a group of formula

 wherein R⁹ and R¹⁰ are independently of each other C₁-C₂₄alkyl, which can be interrupted by one or two oxygen atoms, R²⁵ is H, C₆-C₁₈aryl, C₇-C₁₈aralkyl, or C₁-C₂₄alkyl, R⁴¹ is C₁-C₂₄alkoxy, or C₇-C₁₅phenylalkoxy, and R⁴⁴ is is H, or C₁-C₂₄alkyl.
 10. A 2H-benzotriazole compound of the formula

a is 0, or 1, b is 0, or 1, X¹ is a group of formula

if b is 1, or Y³, if b is 0, wherein c is 0, or 1 X² and X³ are independently of each other a group of formula

wherein d is 0, or 1, Ar¹, Ar², and Ar³ are independently of each other C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted, Y¹ and Y² are independently of each other a divalent linking group, and Y³ and Y^(3′) are independently of each other C₆-C₃₀aryl or a C₂-C₂₆heteroaryl, which can optionally be substituted. 